Surface and Coatings Technology 172 (2003) 308–315
NiTi cladding on stainless steel by TIG surfacing process
Part I. Cavitation erosion behavior
a, a b
F.T. Cheng *, K.H. Lo , H.C. Man
aDepartment of Applied Physics, The Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong, PR China
bDepartment Industrial and Systems Engineering, The Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong, PR China
Received 5 December 2002; accepted in revised for m17 February 2003
Abstract
NiTi was deposited on AISI 316 stainless steel by the tungsten inert gas (TIG) surfacing process, aiming at increasing cavitation
erosion resistance. A thick deposit, with a 750 HV microhardness and dilution ratio of 14% was formed, with strong deposity
substrate interfacial bonding. Small pores (size F20 mm, total volume fraction less than 1%), and some second phase precipitates
were present in the deposit. Even with the presence of such pores, the cavitation erosion rate of the deposit in NaCl solution was
lower than that of AISI 316 by a factor of more than nine, and even lower than that of AISI 316 laser-clad with NiCrSiB, a
co on hard-facing material. The large increase in erosion resistance could be attributed to the partial retention of superelasticity,
and also to the high hardness of the deposit. In this preliminary study on the efficacy of the TIG process for NiTi deposition, the
main proble midentified was the presence of small pores in the deposit, the elimination of which, via more refined processing,
would definitely further increase the cavitation erosion of the deposit.