海藻酸钠调控水热合成羟基磷灰石.doc

  海藻酸钠调控水热合成羟基磷灰石# ** 5 10 摘要：本文用氯化钙和二水合磷酸二氢钠为 Ca 源和 P 源，以尿素的受热分解调整 pH 值， 以海藻酸钠为模板，水热合成出不同形貌的羟基磷灰石。进行了一系列改变海藻酸钠的质量 分数和溶液初始 pH 值的水热合成实验，收集水热产物并对其进行了 X 射线衍射(XRD)、傅 立叶变换红外光谱(FT-IR)和扫描电子显微镜(SEM)物相和形貌表征。结果表明海藻酸钠明显 抑制羟基磷灰石的结晶，且溶液初始 pH 值和海藻酸钠的浓度均对产物的形貌有影响。随着 海藻酸钠浓度的上升，或溶液初始 pH 值的降低，导致构成形貌差异羟基磷灰石晶体的长宽 比逐渐降低。 关键词：羟基磷灰石；水热合成；海藻酸钠 中图分类号：TQ132.3+2 15 Hydrothermal Synthesis of Hydroxyapatite by using alginate WANG Yanming, PENG Wanjia, SU Wen, LI Xudong (Sichuan University,National Engineering Research Center for Biomaterials,Chengdu 610064) Abstract: This article reported the hydrothermal synthesis of hydroxyapatite with different 20 25 30 morphologies by using calcium chloride, sodium dihydrogen phosphate dihydrate, urea and sodium alginate as Ca source, P source, pH regulator, template, respectively. A series of hydrothermal syntheses were conducted by changing the mass fraction of alginate or the initial pH of feedstocks, and the hydrothermal products were collected and characterized by XRD, FTIR and SEM. The results indicated that alginate supressed hydroxyapatite crystallization and that both of the inital pH and alginate concentration had an effect on the morphology of the products. With the increase of sodium alginate concentration or the decrease of initial pH value, the length/width ratio of hydroxypaptite crystals decreased gradually. Key words: hydroxyapatite; hydrothermal synthesis; alginate 0 引言 羟基磷灰石（HAP）是脊椎动物骨骼和牙齿的主要成分。作为生物医学材料，羟基磷灰 [1] [2] 羟基磷灰石是在常温下，pH 值在 4-12 之间最稳定的钙磷化合物 [3] 。羟基磷灰石的合成方法 [4] [5] [6]  35 [7] [8] 水热法是比较成熟的制备羟基磷灰石的方法，产物结晶度较高。通过改变水热条件，如 氯化钙和磷酸二氢钠的浓度、水热温度、水热时间、模板剂量、反应 pH 值，均会对羟基磷 [9] 羟基磷灰石；B. Viswanath 等 [10] 合成出短棒状羟基磷灰石。杨贤燕等 [11] 制备出刺球、薄片 40 状羟基磷灰石。张惠刚等 [12] 合成出花状羟基磷灰石。 海藻酸钠是由 D-甘露糖醛酸和 L-古洛糖醛酸聚合而成的天然多糖，在医学材料中可作 为支架材料 [13,14] ，具有良好的生物相容性。本实验选择水热法，海藻酸钠作为模板调控羟基 磷灰石的生长，初始反应 pH 值和模板剂浓度对产物形貌均有显著影响。 -1- 1 试验部分   45 50 55  1.1 原料与仪器 CaCl2，NaH2PO4·2H2O，尿素，海藻酸钠（均来自 SIGMA 公司,分析纯），去离子水