8R27.弹簧钢晶粒超细化轧制技术研究-东北特殊钢张 宇.pdf

2007 年全国塑性加工理论与新技术学术研讨会 2007 年5 月 沈阳 弹簧钢晶粒超细化轧制技术研究 张 宇 （东北特殊钢集团有限责任公司大连116031） 摘 要：本文根据新型高强、高韧弹簧钢38SiMnVB 的相变点，利用高精度合金钢高速线材连轧机，采用控制轧制 技术生产出超细晶粒钢。通过力学性能对比实验，得出超细晶粒钢比常规轧制钢的力学性能有大幅度提高。同时合 理控制的热轧超细晶粒钢可以不用退火直接拉拔，适用于生产轿车悬挂弹簧或油淬火钢丝。 关键词：弹簧钢；晶粒细化；控制轧制；高强高韧 Study on the Rolling Technology of Super Fine Grain Spring Steel ZHANG Yu (Dong Bei Special Steel group Co ，Ltd Dalian 116031 ) Abstract: According to the point of transformation phase of spring steel 38SiMnVB, super fine grain spring steel is produced by the modern mill and controlling rolling technology and theory. Test match provide that It has not only the super high strength (tensile and yield) but also very high toughness . Hot finished coil rod steel can be cold draw without annealing .Such super fine grain steel is suitable to produce spring of car and quenching wire . Key words: Spring Steel ；Fine Grain ；Control Rolling ； High Strength and Toughness 1 前言 [1] 新一代钢铁材料重大基础研究课题的基本思想是钢的纯净化、均匀化和晶粒超细化 。晶粒细 化显著提高钢的力学性能。随着中国汽车工业的发展，特别是轿车产量的高速增长，对弹簧的质量 提出高强、高韧的要求。弹簧的高强度、高韧性是弹簧材料研究的重要方向[2] 。稳定杆、扭力杆和 螺旋悬挂弹簧对轿车轻量化具有重要意义。38SiMnVB 弹簧钢通过采用微合金化的方法[3]，初步具备 高强、高韧的特性。为了充分发挥该钢种潜能，结合控制轧制理论，研究了微合金弹簧钢的生产工 艺。通过控制轧制获得超细化晶粒，超细化晶粒使钢在超高强度下保持更高的塑韧性。 2 试验材料及生产工艺 2.1 试验材料的主要技术要求 2.1.1 化学成分:试验材料 38SiMnVB 化学成分如表1 所示 表1 试验材料化学成分% Table 1 Chemical compositions of test steel % 元素 C Mn Si V B 主要成分 0.39 1.48 1.21 0.09 0.0019 2.1.2 主要技术要求 （1） 力学性能 热处理后力学性能符合表2 规定。 43 2007 年全国塑性加工理论与新技术学术研讨会 2007 年5 月 沈阳 表2