22R69.低碳高铌HTP钢的动态再结晶数学模型研究-本钢邹天来.pdf

2007 年全国塑性加工理论与新技术学术研讨会 2007 年5 月 沈阳 低碳高铌HTP钢的动态再结晶数学模型研究 邹天来，许云波，王国栋，刘相华 （东北大学轧制技术及连轧自动化国家重点实验室，沈阳） 摘 要：采用 Gleeble-2000 热/力模拟试验机模拟了高 Nb 钢 HTP(High Temperature Processing) 的动态软化行为，并建 立了动态再结晶数学模型，得出了峰值应力、峰值应变与 Z 参数之间的关系，为制定合理的轧制工艺提供实验和理 论依据。 关键词：数学模型；HTP ；动态再结晶 Research of Dynamic Recrystallization Modeling for High Nb Micro-alloyed Steels ZOU Tianlai, XU Yunbo, WANG Guodong, LIU Xianghua (The State Key Lab of Rolling Technology and Automation, Northeastern University, Shenyang) Abstract: Dynamic recrystallization action of high Nb micro-alloyed steels has been simulated by Gleeble-2000 thermal/mechanical simulation tester. Dynamic recrystallization modeling has been developed. The relationship of Peak stress, peak strain and Z parameters has been investigated. Research results can provide some advice for high Nb micro-alloyed steel rolling. Key words: mathematical modeling, high temperature processing, dynamic recrystallization 1 前言 由于金属热变形中内部组织结构的变化非常复杂,对于低碳高铌HTP钢流变应力的预测也就较为 困难。探讨热轧轧制过程中的组织演变行为是研究其组织与性能预报的重要内容之一。在热轧过程 中主要的微观组织变化可分为三类,一是动态变化,即变形过程中发生的加工硬化和动态回复或动态 再结晶；二是静态变化,即轧制间歇时间内静态回复或静态再结晶、晶粒长大;三是介于动态和静态之 间的状态变化,即亚动态再结晶。影响再结晶行为的因素很多,其发生都有一定的条件。 本文以低碳高铌HTP钢为研究对象,在热模拟实验的基础上,分析了该钢种高温变形时动态再结 晶行为,对该钢种高温轧制过程中动态再结晶数学模型进行了探讨。 2 实验材料及方法 测试样品主要化学成分 （质量分数，% ）为：0.024C，0.099Nb，0.169Si，1.49Mn，0.011Ti，0.027Al， 0.26Cu，0.154Ni 。将板材加工成φ8mm×15mm的圆柱形试样。本实验在Gleeble2000热模拟试验机上 进行。采用单道次压缩，测试真应力-真应变曲线。 将试样以20 ℃/s 的速度加热到1200℃，保温3分钟后以10℃/s的速度冷却到不同温度，保温30s 以 消除试样的温度梯度，然后进行压缩变形，变形温度范围为800～1150℃，应变速率分别为0.01、0.1、 1.0和5.0s-1 ，应变量为1.0。具体实验工艺见图1。 128 2007 年全国塑性加工理论与新技术学术研讨会 2007 年5 月 沈阳