合成绝缘子硅橡胶伞群材料老化特性与其红外光谱研究.pdfVIP

合成绝缘子硅橡胶伞群材料老化特性及 其红外光谱研究 陈晓春，郑敏聪，李建华 安徽省电力科学研究院，安徽省合肥市 230601 Aging Characteristics of Silicone Rubber Composite Insulator Sheds studied by IR Spectroscopy Chen Xiaochun, Zheng Mincong, Li Jianhua Anhui Electrical Power Research Institute, Anhui Hefei, 230601 ABSTRACT: Aging characteristics of silicone rubber 1 引言 composite insulator shed materials obtained from 一直以来，环境污染引起的外绝缘闪络 long-term operation and laboratory aging experiments 事故严重威胁我国电力系统的安全运行，为 were studied by ATR-FTIR. The results show that 了有效防止输变电设备外绝缘的污闪问题， long-term operation-aged silicone rubber exhibit 硅橡胶合成绝缘子的研究和应用得到了越 various main chain fragmentation, cross-linking 来越多的关注与重视。各类合成绝缘子，在 degree decrease, methyl groups loss, etc.. 600h 不同的运行环境下已经积累了 30 多年的运 exposure of silicone rubber samples to UV irradiation 行经验。运行中，合成绝缘子由于其有机材 leads to the decrease of organic components in silicone 料的特性，不可避免的会出现老化问题，主 rubber, while ATH remains nearly untouched. 500h 要表现为外绝缘材质的劣化。外绝缘材质的 exposure of silicone rubber samples to salt mist causes 劣化一般并不直接导致绝缘子的电气或机 the decrease of ATH, while organic components in 械负荷功能的丧失，但如果老化作用积累到 silicone rubber remains the same as before. 一定的程度，就会发生从量变到质变的突 KEY WORD: ATR-FTIR spectroscopy ； composite 跃，导致合成绝缘子损坏，丧失其正常的机 insulators ；silicone rubber ； aging 械或者电气复合承载能力，往往造成绝缘子 掉串、导线落地、电力中断等恶性事故。 摘要：文中通过 ATR-FTIR 分析，研究了运行老化 深入研究硅橡胶伞群材料在长期运行 和试验室人工加速老化条件下硅橡胶的老化特性。 应力下以及实验室模拟单因素作用下的老 结果表明运行老化的合成绝缘子伞群材料出现有不 化特性和机理，是绝缘材料状态诊断和检测 同程度的主链断裂、交联度下降以及侧链甲基减少 的基础。本文采用表面衰减全反射红外光谱 的现象；紫外作用 600h 导致硅橡胶的有机成分含量 （ATR-FTIR ）分析法，对 110 KV、500 KV 有所下将，但对于无机阻燃剂填料 Al(OH)3 （ATH ） 交流线路运行 15 年左右的合成绝缘子伞群 的影响不大；盐雾作用 500h 后的硅橡胶主链、侧甲 材料以及人工加速紫外老化和盐雾老化作 基无明显变化，但 ATH 的含量有稍许降低。