壳聚糖论文：壳聚糖 聚己内酯 共混薄膜 蛋白质粘附 纤维粘连蛋白 细胞行为.docVIP

壳聚糖论文：壳聚糖/聚己内酯共混膜的制备及性能研究 【中文摘要】本研究将不同质量比的壳聚糖(Chitosan)和聚己内酯(PCL)共混溶液通过旋转涂膜仪制备成为均匀薄膜。共混薄膜表面的形貌特征和亲疏水性分别通过原子力显微镜和滴形分析仪加以检测。牛血清纤维粘连蛋白(FN)在壳聚糖/聚己内酯薄膜表面的粘附行为通过石英晶体天平进行表征。小鼠成纤维细胞(3T3)在薄膜表面的粘附行为通过MTT法得以检测。实验结果表明,壳聚糖/聚己内酯薄膜表面的形貌特征和亲疏水性在很大程度上取决于两者在共混溶液中的质量比。在壳聚糖/聚己内酯薄膜表面粘附的牛血清纤维粘连蛋白和3T3细胞随着薄膜中壳聚糖含量的增加而减少。与此相反,生长在壳聚糖/聚己内酯薄膜上的3T3细胞形貌和细胞骨架随着薄膜中壳聚糖含量的下降而逐渐被抑制。 【英文摘要】In this study, chitosan/poly(ε-caprolactone) (PCL) blend films with different mass ratios were prepared by spin coating with chitosan/PCL mixture solution. The surface topography and hydrophilicity of the blend films were examined with Atomic Force Microscopy (AFM) and Drop Shape Analyzer (DSA), respectively. The adsorption of fibronectin (FN) on the blend films surface was detected by Quartz Crystal Microbalance (QCM). The adhesion and cell morphology of mouse fibroblast cells (3T3) on the films were also ... 【关键词】壳聚糖 聚己内酯 共混薄膜 蛋白质粘附 纤维粘连蛋白 细胞行为 【英文关键词】Chitosan Poly(ε-caprolactone) Blend films Protein adsorption Fibronectin Cell behavior 【索购全文】联系Q1：138113721 Q2：139938848 同时提供论文写作一对一辅导和论文发表服务.保过包发 【目录】壳聚糖/聚己内酯共混膜的制备及性能研究 摘要 4-5 Abstract 5 目录 6-7 1. 绪论 7-20 1.1. 生物材料 7-11 1.2. 生物相容性 11-15 1.3. 壳聚糖和聚己内酯 15-16 1.4. 本研究的重点 16 1.5. 纤维粘连蛋白 16-17 1.6. 3T3细胞 17-18 1.7. 石英晶体天平 18-20 2. 实验方法 20-27 2.1. 壳聚糖/聚己内酯薄膜的制备 20-21 2.2. 对不同壳聚糖/聚己内酯薄膜的表面形貌分析 21 2.3. 对不同壳聚糖/聚己内酯薄膜表面接触角(Contact Angle)分析 21-22 2.4. 纤维粘连蛋白在不同壳聚糖/聚己内酯薄膜上的粘附 22-24 2.5. 3T3细胞在不同壳聚糖/聚己内酯薄膜表面的粘附和增殖活性 24 2.6. 壳聚糖/聚己内酯薄膜表面生长的3T3细胞形貌和细胞骨架 24-26 2.7. 数据统计处理 26-27 3. 实验结果和讨论 27-38 3.1. 壳聚糖/聚己内酯薄膜表面形貌分析 27-28 3.2. 壳聚糖/聚己内酯薄膜表面的接触角分析 28-30 3.3. 牛血清纤维粘连蛋白在壳聚糖/聚己内酯薄膜表面的粘附分析 30-31 3.4. 壳聚糖/聚己内酯薄膜表面粘附的牛血清纤维粘连蛋白解吸附(Elution)分析 31-33 3.5. 细胞在壳聚糖/聚己内酯薄膜表面粘附及增值率分析 33-35 3.6. 3T3细胞在壳聚糖/聚己内酯薄膜表面伸展形貌和细胞骨架观察 35-38 4. 结论及创新点 38-39 参考文献 39-46 在校期间发表论文及科研成果清单 46-47 致谢 47