AlPbα-PbO2复合惰性阳极材料的电化学合成.pdfVIP

Trans. Nonferrous Met. Soc. China 25(2015) 2095−2102 Electrosynthesis of Al/Pb/α-PbO composite inert anode materials 2 Gang HU1,2 1,2 2 2 3 2 2 , Rui-dong XU , Shi-wei HE , Bu-ming CHEN , Hai-tao YANG , Bo-hao YU , Qiang LIU 1. State Key Laboratory of Complex Nonferrous Metal Resources Clean Utilization, Kunming University of Science and Technology, Kunming 650093, China; 2. Faculty of Metallurgical and Energy Engineering, Kunming University of Science and Technology, Kunming 650093, China; 3. State Key Laboratory of Multi-Phase Complex Systems, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100190, China Received 16 August 2014; accepted 10 January 2015 Abstract: The α-PbO deposition layers were prepared on the surface of Al/Pb substrates by constant current electrosynthesis from 2 an alkaline bath, and Al/Pb/α-PbO2 composite inert anode materials were obtained. The effects of the bath composition and bath temperature on the electrosynthesis of α-PbO2 were investigated by means of anodic polarization method, the phase structures and surface microstructures of Al/Pb and α-PbO2 deposition layers were tested by means of X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. The experimental data have shown that the process of α-PbO2 formation have several stages. The