特点 LRM母胶应用在轿车胎的胎面胶中 可降低轮胎滚动阻力至A或B级 抗湿滑性能达到C级以上 同时具有优异的拉伸强度和抗撕裂强度 具有较低的门尼粘度和较长的焦烧时间有利于生产加工 可混合使用或独立使用 超低滚阻产品 TOPWIZ? LRM 性能 使用LRM超低滚阻胶料，门尼粘度低，加工性能优异，降低加工成本；门尼焦烧时间增加，提高加工安全性。LRM超低滚阻胶料在保持适当硬度的同时， 其tand值比传统绿色轮胎配方低一半以上，能够大幅度降低滚动阻力。根据设计需要，胶料的Tg可在为-30℃到-10℃之间调节，胶料的硬度可在55-65之间调节。LRM超低滚阻胶料，具有优异的拉伸强度和抗撕裂强度。 加工性能 门尼粘度 ML(1+4)100℃ 门尼焦烧 130℃（分钟） 硬度ShoreA 性能 硫化胶性能 LRM超低滚阻胶料在保持适当硬度的同时， 其tand值比传统绿色轮胎配方低一半以上，能够大幅度降低滚动阻力。根据设计需要，胶料的Tg可在为-30℃到-10℃之间调节，胶料的硬度可在55-65之间调节。 性能 LRM超低滚阻胶料，具有优异的拉伸强度和抗撕裂强度。 抗破坏性能 拉伸强度（MPa） 撕裂强度（N/mm） 损耗因子tand相对值 产品 项 目 LRM-100 技 术 参数 门尼粘度ML(1+4) 75 Tg（℃） -17.0 105°C加热减重 （%） ＜0.6 母胶组分 （%） 溶聚丁苯橡胶、白炭黑、特种助剂 产品 应用 LRM-100 滚动阻力达到A-B级水平 LRM-A 滚动阻力达到A+级水平 Features LRM for PCR tire tread Reduce tire rolling resistance to achieve EU level A or B Wet grip achieve EU level C or above Excellent tensile strength and tear resistance Suitable Mooney viscosity and scorch time for easy processing Can be used independently or blended with other compounds Ultra Low Rolling Resistance Product TOPWIZ? LRM Performances The LRM has low Mooney viscosity and good processability which reduces production cost.The longer scorch time enhances the processing safety. LRM compound can reduce tand value more than 50% from that of the conventional green tire tread compound with suitable rigidity level for ultra low rolling resistance tires. According to requirements, the compound Tg can be adjusted between -30 ℃ to -10℃ and its ShoreA hardness is adjustable between 55 to 65. LRM compound has excellent tensile strength and tear resistance. Processability ML(1+4)100℃ Scorch time 130℃ (min) ShoreA Hardness Performances Cured properties LRM compound can reduce tand value more than 50% from that of the conventional green tire tread compound with suitable rigidity level for ultra low rolling resistance tires. According to requirements, the compound Tg can be adjusted between -30 ℃ to -10℃ and its ShoreA hardness is adjustable between 55 to 65. Performances LRM compound has excellent tensile stre