难处理金矿焙砂氯化挥发提金试验研究郭持皓袁朝新刘大学胡磊（北京.docVIP

难处理金矿焙砂氯化挥发提金试验研究 郭持皓 袁朝新 刘大学 胡磊 （北京矿冶研究总院，北京 100160） Chloride Volatilization Study on Gold Recovering From calcine of Refractory Gold Ore GUO Chi-hao YUAN Chao-xin LIU Da-xue HU Lei (Beijing General Research Institute of Mining ＆MetallurgyBeijing 100160,China) 摘要：采用高温氯化挥发法对难处理金矿的焙砂进行提金试验研究，试验考察了氯化温度氯化氯化量在氯化温度1150、1h、CaCl2添加量5%的条件下，Au、Ag的挥发率分别达到约98%、60%SiO2、Al2O3、CaO、MgO和FeAu、Ag等有价元素与脉石成分分离 关键词：难处理金矿，焙砂，氯化挥发，造球，无氰； 中图分类号：TF803.2 文献标识码：A 文章编号： Abstract: A test of pelletizing- chloride volatilizing was performed on calcine of refractory gold ore and factors effecting gold volatilization rate and pellet strength were investigated. Results indicated that under optimum conditions as: roasting temperature of 1150℃, roasting time of 1h, CaCl2 addition rate of 5%, volatilization rate of gold and silver can reach around 98% and 60% respectively while iron and gangue components of SiO2, Al2O3,CaO and MgO basically remain in fired pellet. Based on the result, a new process of recovering gold from calcine of refractory gold ore by chloride volatilization was developed. Keywords: refractory gold ore；calcine；volatilization；pellet-making；cyanide-free； 郭持皓(1978),男（汉）,江苏徐州,高级工程师,硕士,9578guo_chh@ 基金项目：国家高技术研究发展计划（863计划）项目（2011AA06A104）,课题名称:氰化渣硫铁金梯级分离富集与无害化技术.1 前言 针对加压氧化细菌氧化对和环境造成和污染等缺点 2 试验 2.1 原料 本次试验的原料为粒级分布与每个粒级含Au、Ag量分析 表1 焙砂化学分析 Chemical analysis of Calcine 元素 Au/g/t Ag/g/t As S C Cu Pb Zn 含量,% 44 46.6 0.64 1.12 0.17 0.049 0.048 0.15 元素 Fe SiO2 CaO MgO Al2O3 K2O Na2O — 含量,% 23.24 49.62 2.01 1 7.47 2.51 0.22 — 表2 焙砂粒级分布与每个粒级含Au、Ag量分析 粒度 每个粒级情况 Au含量情况 Ag含量情况 重量/g 百分比/% Au（g/t） 百分比/% Ag（g/t） 百分比/% +120 23.2 11.7 69 16.91 63.58 14.75 -120～+200 56.2 28.3 36.17 21.48 55.13 30.98 -200～+300 53.3 26.9 44 24.78 49.84 26.56 -300～+400 12.1 6.1 62.5 7.99 43.47 5.26 -400 53.7 27.1 50.83 28.84 41.83 22.46 总计 198.5 100.0 — 100.00 — 100.00 主要试验设备：马弗炉、TJ-1400C高温气氛管式炉、棒磨机、圆盘制粒机、回转窑、WDS-10型电子式拉（压）力试验机和电子天平等。 主要试剂：膨润土、氯化钙等。 2.3 试验方法 焙砂磨矿至一定粒度加入膨润土