中间包永久层用耐材.docVIP

中间包永久层用耐材Refractories used in the tundish safety lining 高铝浇注料是以高铝莫来石原料为主，以水泥或微粉为结合剂的不定型产品，具有强度高，特别是中温强度高，热震性好的特点。在中间包中采用高铝莫来石预制块和铝锆预制块替代高铝浇注料能明显提高使用寿命，提高中间包使用的安全性。 Using high alumina mullite as rawmaterial, cement or micro-powder as binding agents, the Hi-Al2O3 castables is one unshaped refractory and has the benefits of high strength,especially under medium temperature, and good thermal shock resistance. Substituting high alumina castables with high alumina mullite or Al2O3-ZrO2 based precast block can extend the tundish lifespan and enhance the security in the service. 项目Item 高铝浇注料High Alumina Castables 高铝莫来石预制件High alumina mulite precast block 铝锆预制件Al2O3-ZrO2 precast block CHA-2A CHM-4SB LZ-1A 体积密度Bulk Density g/cm3 110℃×24h 2.68 2.85 3.05 耐压强度Cold Crushing Strength MPa 110℃×24h 64.5 60.5 60.0 1500℃×3h 85.7 ≥70 90.0 抗折强度Modulus of Rupture MPa 110℃×24h 7.0 - 9.2 1500℃×3h 12.0 12 12.5 残余线膨胀Residual Linear Change % 1500℃×3h +.48 +0.25 +0.13 化学成份Chemical Composition % Al2O3 68.50 80.00 78.00 ZrO2 - - 5.20 SiO2 15.6 7.35 - 使用部位 Application 侧墙Side Wall 非渣线Non-slagline 渣线Slag Line 铁水包用铝碳化硅碳不烧砖 铁水包用铝碳化硅碳砖是以刚玉、铝矾土、石墨、碳化硅为主要原料，经低温烘烤而成的不烧制品，产品具有较好的抗侵蚀性、耐剥落性和蠕变性。 Al2O3-SiC-C Brick is based on corundum, bauxite, Graphite, Siliconcarbide, bonded by resin. It is suitable for general use in the working lining of torpedo car or hot metal car, the high purity carbon and corundum provide excellent resistance to highly corrosion, spalling and creep. 项目Item ADL30RS2 ADL40RS ADL50RS ADL60RS-3F ADL60RS-3K-2 ADL60RS-5K 显气孔率Apparent Porosity % 8.5 8.0 7.5 8.5 7.3 7.4 体积密度Bulk Density g/cm3 2.6 2.6 2.7 2.8 2.9 2.8 耐压强度Cold Crushing Strength MPa 50 50 50 50 60 55 化学成份Chemical Composition % Al2O3 38.00 38.7 43.0 51.0 54.5 58.2 SiC 4.50 4.18 4.50 4.50 9.30 11.30 C 11.50 11.80 10.50 11.50 13.40 4.60 使用部位Application 铁线/包底Metal Line/Barrel 铁线/包底Metal Line/Barrel 铁线/包底Metal Line/Barrel 铁线/包底Metal Line/Barrel 铁线高强度品M/L High Strength 铁线Me