医用HA-βTCP复合合成技术进展与分析报告.docVIP

化工技术进展与研究课题综述 医用HA/β-TCP复合材料合成技术进展与研究 四川大学化工学院 学生姓名：王明光 学 号：1143084124 专 业：化学工程与工艺 指导老师：罗仕忠  摘要 目前通过人工合成的HA/β-TCP复合生物材料因其具备优良的特性已作为人工骨材料及组织材料得到了广泛的应用。医用双相磷酸钙(β-TCP)陶瓷是β磷酸三钙(β-TCP)和羟基磷灰石(HA)的复合体，其成分与骨矿物组成类似。它具有良好的生物相容性，在生物医学领域具有非常广阔的应用前景，且在生理环境下能发生不同程度的降解,被组织吸收。医用双相磷酸钙复合材料的合成方法主要有湿法工艺、干法工艺、水热法工艺及溶胶凝胶法工艺等。 Abstract Currently HA/β-TCP βioceramic composites with excellent characteristics βy its artificially synthesized has βeen widely used as a βone suβstitute material and the tissue material.Medical βiphasic calcium phosphate (β-TCP) ceramic is a kind of composite materials composed βy βtricalcium phosphate (β-TCP) and hydroxyapatite (HA) , its composition is similar to the composition of βone mineral.It has good βiocompatiβility, in the βiomedical field has a very βroad application prospects, and in the physiological environment can occur in varying degrees of degradation, is aβsorβed βy tissue.The synthetic methods of m edical βiphasic calcium phosphate composites are mainly the wet process, the dry process ,the hydrothermal method process and sol-gel processes ,and so on . 关键词 HA；α-TCP；β-TCP；生物性能；合成技术方法与改进 前言 植骨材料 (βone graft suβstitute)在骨科以及头颈外科、口腔颌面外科等有着广泛的临床需要，临床常用的植骨材料包括自体骨、异体骨(包括异体冻干骨和异体脱矿骨基质 Demineralized βone Matrix，DβM )、骨形成蛋白(βMP)和各类人工骨[1]。目前，自体骨仍然是最有效的主要植骨材料来源，但由于取骨量有限和取骨带来的诸多并发症，限制了其临床应用。异体骨则存在着感染、传播疾病、免疫原性、成骨能力以及质量因供体不同而差异较大等问题，而且骨源有限、价格昂贵。骨形成蛋白具有骨诱导活性和优异的成骨性能，但缺乏骨传导活性和力学强度，大多通过基因工程得到，价格极其昂贵，并需要与载体复合使用。因此，研究各类人工植骨代材料，以克服自体或异体骨固有的缺点，是临床迫切需要解决的问题。 理想植骨材料应该具有以下特点：良好的生物相容性；生物可吸收性；骨传导性；骨诱导性；结构与骨相似并且性价比高、易于操作使用。临床常用植骨材料按主要成分可以分成磷酸钙类和硫酸钙类2种。其中，磷酸钙类植骨材料与骨组织的矿物相组成和性质最为接近。 自从20世纪70年代起，磷酸钙类生物陶瓷开始显露头角,并且不断取得突破性进展。生物陶瓷材料的研究及临床应用,已经从短期的替换和填充发展为永久牢固性种植,从生物活性材料发展到生物活性的材料及其多相复合材料,从生物材料的研究发展到组织工程的研究。生物活性陶瓷在生理环境中可通过其表面发生的生物化学反应与人体组织形成化学键性结合。主要包括羟基磷灰石(HA)、磷酸三钙(β-TCP)及聚磷酸钙（CPP）等可降解吸收陶瓷。可生物降解磷酸钙陶瓷具有以下优点：[2] (1)最终无异物存留； (2)材料完全吸收后所形成新骨的塑型不再受材料存在的影响； (3) 材料吸收形成的新骨塑型后强度优于新骨与材料结合的强度。 说明：本文将综述HA、TCP、不同配比的复合BCP材料性能，及HA、T