M705-GRN360-K.pdf

M705-GRN360-K TC-P11-1.3E Feb.2003 －1 Senju Metal Industry Co.,LTD. Pb Senju Metal Industry Co.,LTD. High-Reliability Pb-Free Solder Paste M705-GRN360 K-Series 23 Senju Hashido-cho, Adachi-Ku, Tokyo, Japan. Phone: (81)-3-3888-5156 Fax: (81)-3-3870-3032 Senju Metal Industry Co.,Ltd. Manufacturer M705-GRN360-K TC-P11-1.3E Feb.2003 －2 Senju Metal Industry Co.,LTD. Pb Pb-free solder’s introduction into production lines continues to protect the earth’s environment. ECO-solder paste M705-GRN360-K series was developed with this in mind along with the requests of customers who have been using M705 Pb-free paste. Former versions had heat resistance in high temperature reflow, a control of solder balling and high reliability. However this new series carries out improvements in many areas: stability of viscosity in storage and in use; the color tone of flux residue; improvement in flux residue cracking; improvement in further preventing side balling; joint appearance (cosmetic); and improvement in wettability to poor wetting components. M705 (Sn-3.0Ag-0.5Cu) is considered to be a standard Pb-free alloy. Please ask separately about combination with other alloys. M705-GRN360-K Series 63Sn-PbM705 23.521.7CTE (ppm/C) 45.839.40.2% Yield point (MPa) 16.617.9Vickers Hardness (Hv) 41.6 46 53.3 220 219 217 7.4 Ag3.0-Cu0.5-Sn_Balance 26.3Young’s module (GPa) 59Elongation(%) 56.0Tensile strength (Mpa) Liquidus Peak 183 Solidus Melting temperature (C) 8.4Specific gravity Sn63-Pb_BalanceAlloy Composition(%) A characteristic of M705 alloy SEM Photo of M705 powder This powder is a globular form, and has very little surface oxidization. Such is the case with all ECO-solder paste products from Senju Metals. (This picture shows type-4(25-36um) as a reference) M705-GRN360-K TC-P11-1.3E Feb.2003 －3 Senju Metal Industry Co.,LTD. Pb M705-GRN360-K characteristics JIS Z 3197PASSCopper plate corrosion test Solder Paste FLUX Solder Powder Titration method0.0%/FluxHalogen JIS Z 31