喷嘴的熔模铸造生产工艺研究.pdf

维普资讯 学兔兔 Jan．2008 VOI．57 NO．1 帅 · 23 · 圈 喷嘴的熔模铸造生产工艺研究 邵抗振，李 桐，赵竞翔 (郑州机械研究所，河南郑州450052) 摘要：重点介绍了喷嘴的熔模铸造基本．~q一4-过程和主要工艺参数。结果表明，该工艺合理可行，解决了该产品普通铸造 中的铸造缺陷问题。不但成功生产出了高质量的产品，提高了产品的合格率，而且还为同类产品的熔模铸造提供了参考。 关键词：喷嘴；熔模铸造；工艺参数 中图分类号：TG249．5 文献标识码：B 文章编号：1001—4977(2008)Ol一0023—02 Production Technology of I nvestment Casting Nozzles SHAO Kang—zhen，LI Tong，ZHAO Jing—xiang (Zhengzhou Research Institute of Mechanical Engineering，Zhengzhou 450052，Henan，China) Abstract： The basic technical process and main processing parameter of investment casting nozzles are presented in detail．The results showed that the process iS reasonable and feasible．and the product defects appearing in sand casting are removed．Not only the high quality products are produced successfully and percent of pass iS enhanced．but also the reference iS provided for like products by investment casting． Key WOrds：nozzle；investment casting；processing parameter 喷嘴是国外某大公司消耗量较大的铸件，其结构 1 生产条件 复杂，精度要求高。铸件重14 kg，厂家要求该产品材 质为PHI7—4，是一种控制相变型沉淀硬化不锈钢，牌 生产过程中使用的都是生产上常见的熔模铸造设 号为0Cr17Ni4Cu4Mo。此钢耐腐蚀性能优于一般的马 备，包括M225系列射蜡机、MFS60浮砂筒、ZL50沾浆 氏体不锈钢。由于该产品表面不加工，因此表面质量 机、DN800／1000电热脱蜡机、YJX100xl00一I2RF焙烧 要求较高，要达到平整光滑，即无裂纹、无鼓包、夹 炉和KYPS l 50 kg中频感应炉。 渣、气孑L等缺陷；同时内部无缩松、缩孑L，组织致密 由于喷嘴表面不需要加工，根据喷嘴的结构特点， 等。由于普通铸造很难达到表面质量要求，所以特研 为了减少生产过程中铸件变形，选用石蜡硬脂酸低温 究了喷嘴的熔模铸造生产工艺，与同行交流。 蜡料生产蜡件。喷嘴材料化学成分如表l所示。 表1 喷嘴材料化学成分 Table 1 Chemical compositi