炼铁合金感应炉用Al2O3基复合耐火材料的研究.pdfVIP

学兔兔 Sep．2008 · 950· Vo1．57 NO．9 炼铁合金感应炉用AI2O3基复合耐火材料的研究 武志红，杨晓凤，徐长海，薛群虎 (西安建筑科技大学材料学院，陕西西安7l0o55) 摘要：以刚玉和电熔镁砂为原料，采用干式捣打法制得了含镁铝尖晶石的复合耐火材料，探讨了 ；~nCrzO，粉及ZrO：粉 对材料性能的影响，XRD结果表明，产物的物相组成为MA，采用静态侵蚀法对试样进行抗侵蚀试验。结果表明，以刚 玉和电熔镁砂为原料制得的复合材料，具有较高的耐压强度和抗侵蚀能力；添~Cr20 粉比添]j~ZrO 粉具有明显的提高 材料性能的效果。 关键词：刚玉；镁砂；镁铝尖晶石；铁合金 中图分类号：TF065．1+3 文献标识码：A 文章编号：1001—4977(2008)09—0950—03 Study on Alumina Composite Refractory Used in Induction Furnace for Melting Ferroalloy WU Zhi—hong，YANG Xiao—feng，XU Chang—hai，XUE Qun-hu (School of Material Sci．and Eng．，Xi’an Univ．of Arch．Tech．，Xi’an 710055，Shaanxi，China) Abstract：A new type of aluminum composite refractory containing MA spinel was produced by dry-ramming．The effects of Or203 or Zr02 addition on the properties of composite refractory were investigated．X．ray diffraction(XRD)results indicate that the final products consisted of MA．The anti-corroding capability of product was analyzed by means of static-corroding method．The experiments results showed that the com posite refractory has high—pressure resistance and corrosion resistance．The properties of the refractory were more greatly improved by adding 0r203 than that of adding Zr02． Key words：corundum；magnesia；magnesia alumina spinel；ferroalloy 在熔炼铁合金的过程中，耐火材料的成分对铁合 火材料的抗侵蚀性、热振稳定性及熔炼温度的高要求 金的质量有显著影响，包括铁合金纯度、铁合金的成 等原因。因此，在高纯氧化铝基体中加入镁石、铬矿 分控制等方面。以前的研究偏向于把注意力集中在渣 以及尖晶石质材料对材料进行优化是可行的方法[2]。 对耐火材料的影响，实际上，铁合金、渣和耐火材料 1 试验原料及配比 的成分是一个多项反应的耦合体系，不仅耐火材料和 渣