含镍元素耐硫酸露点腐蚀钢的开发与应用.pdfVIP

含镍元素耐硫酸露点腐蚀钢的开发与应用 doi ：10.3969/j .issn.1006-110X .2016.04.004 含镍元素耐硫酸露点腐蚀钢的开发与应用 张 霞 ，王成建 ( 天津钢铁集团有限公司技术中心，天 津 300301) [摘 要 ] 为满足市场需求,通过制定合理的炼钢、连铸、轧钢工艺流程，开发出含镍元素耐硫酸露点腐蚀钢。其表面 质量良好、夹杂物控制级别低，通过添加镍元素，降低了耐腐蚀钢中铜元素在晶界处的富集，有效阻止了发生铜脆的 可能性，保证了产品质量,能够满足生产要求。 [关键词] 耐硫酸露点腐蚀钢；镍 ;铜脆;开发 Development and Application of Sulfuric Acid Dew Point Corrosion Resistant Nickeliferous Steel ZHANG Xiaand WANG Cheng-jian (Technology Center of Tianjin Iron and Steel Group Co., Ltd., Tianjin 300301, China) Abstract In order to fulfill market demand, sulfuric acid dew point corrosion resistant nickeliferous steel was developed by formulating reasonable steel-making, casting and rolling processes. Its surface quality was good and inclusion level low. With the addition of nickel element, the enrichment of copper at grain boundary for corrosion resistant steel was reduced, which effectively prevented the possibility of copper brittleness. The product quality was ensured and production requirement could be met. Key words sulfuric acid dew point corrosion resistant steel; nickel; copper brittleness; development i 引言 钝化膜，起到了抗硫酸腐蚀的作用[11。但在实际生产 耐硫酸露点腐蚀用钢主要应用于高含硫烟气 与加工中，含 Cu钢的铜脆现象是不可回避的问题。 中的省煤气、空气预热器、热交换器和蒸发器，以抵 一方面，Cu元素的液化析出温度为1 083益，比钢 御含硫烟气的结露腐蚀，提高了电力石化领域设备 的熔点低很多，高温下熔化的铜在钢中沿晶界渗透 的使用寿命和生产效率，符合国家对企业节能减 扩散，严重时会使被加热的钢在锻造时出现星形裂 排、绿色生产的要求，具有良好的市场前景及开发 纹而报废。另一方面，由于铜比铁难氧化，当钢中含 价值。为加快企业转型升级，改善产品结构，进一步 铜量大于0 .20% 时，将钢加热到 1100耀1 200 益，氧 提高高端产品比例，天钢以市场需求为导向，成功