纳米陶瓷复合进展_闫联生.doc

纳米陶瓷复合材料研究进展 闫联生 余惠琴 宋麦丽 王 涛 (陕西非金属材料工艺研究所, 西安 710025) 文 摘 介绍了纳米陶瓷复合材料的研究进展,包括纳米陶瓷复合材料的制备工艺 、材料性能、纳米补强增韧机理以及纳米与传统补强增韧方法并用技术。 关键词 纳米陶瓷复合材料, 性能 ,制备工艺 Research Development of Ceramic Nanocomposites Yan Liansheng Yu Huiqin Song Maili Wang Tao (Shaanxi Institute of Non-metallic Material and Technology , Xi' an 710025) Abstract Mechanical properties of ceramic nanocomposites , such as strength , toughness and creep ,are superior to that of traditional ceramics .Ceramic nanocompositing has become an effective way to improve the mechanical properties of traditional ceramics .Research development fields of ceramic nanocomposites are reviewed ,which include processing and properties of the ceramic nanocomposites ,reinforced/toughened mechanism of nanoparticles ,and commingled reinforced/ toughened techniques of the nanoparticles and traditional reinforcements . Key words Ceramic nanocomposite ,Property ,Fabrication 1 前言 [ 图 1(d)] , 将使复合材料产生一种全新的性能, 如 纳米技术一经出现, 便在改善传统陶瓷材料性 具有象金属材料一样的可加工性和超塑性等 ,但有 能方面显示出极大的优势。加入纳米相复合后陶瓷 关这种纳米-纳米型陶瓷复合材料的研究还未见报 材料的室温强度和韧性大为提高 ,高温强度和抗蠕 道 ,目前仅见过超塑性单相纳米陶瓷材料的报道 ,如 变性能也有显著改善, 如加入 15 %纳米 SiC , 可使 纳米 SiC 材料在 1 800 ℃的拉伸变形可达 140 %[ 2] , Al2O3 材料的强度由350 MPa 提高到1 500 MPa[ 1] , 引 纳米ZrO2 材料的室温拉伸变形可达 300 %[ 1] , 远高 起了世界的高度重视, 在世界范围内兴起纳米陶瓷 于传统的陶瓷材料。 复合材料研究热潮 ,纳米陶瓷复合材料的基础研究 和应用研究都取得了重大进展。 2 纳米陶瓷复合材料的分类 根据纳米相在复合材料中的分布情况, 纳米陶 瓷复合材料分晶内型、晶间型、晶内 —晶间混杂型和 纳米—纳米型, 如图 1 所示。通常制备的纳米陶瓷 复合材料多为晶内—晶间混杂型[ 图 1(c)] , 纳米颗 粒分散在基体的晶粒内和晶界上。纳米 —纳米型复 合材料是由纳米颗粒分散剂和纳米基体晶粒组成如 (a) 晶内型 收稿日期:2001 -04 -18 闫联生, 1968 年出生, 硕士, 主要从事复合材料的应用研究工作  — 6 — 宇航材料工艺 2003 年 第 1 期  (b) 晶间型 (c) 晶内—晶间混杂型 (d) 纳米—纳米型图 1 纳米陶瓷复合材料的分类 Fig .1 Classification of ceramic nanocomposites 纳米陶瓷复合材料的制备技术 .1 机械混合法[ 3] 机械混合法是最早出现的一种纳米陶瓷复合材料制备技术 ,制备方法是将纳米粉末和基质粉末混合,球磨后烧结成型;其优点是工艺简单, 但由于球磨本身不能完全破坏纳米颗粒之间的团聚, 不能保证纳米相和基质相的均匀分散 , 同时由于球磨介质的磨损,会带入一些杂质 ,给纳米复合材料性能带来不利影响。为此在机械混合的基础上使用大功率超声振荡以破坏团聚, 并使用适量分散剂 ,提高分散均匀性。球磨介质采用与基质相同的材料, 可减少因球磨带来的杂质 ,如制备纳米 SiC 粉末增强 Si3N4 基 陶瓷复合材料采用 Si3N4 磨球。 3 .2 复合粉末法[ 4～ 12