浇注型聚氨酯弹性体胶辊的加工工艺（Processing technology of casting polyurethane elastomer roll）.docVIP

浇注型聚氨酯弹性体胶辊的加工工艺（Processing technology of casting polyurethane elastomer roll） Processing technology of casting polyurethane elastomer roll PAN surface finishing: turning or grinding on processing equipment as required. (4) pay attention to the main points: The die structure is reasonable, the assembly can be *, the parting surface has no leakage, and the glue can leak. The temperature balance requires that the temperature of the die, the roller core and the rubber material are basically the same, and the temperature of each part of the mold is basically the same. The pouring point glue in roll core or mold edge should remain fixed, with no air bubbles is appropriate, in order to prevent coerced bubbles, the mold can be appropriately tilted along the wall and make rubber. Before the rubber roller does not reach the mold strength, do not move the mold at will, in case of crazing. When assembling moulds and rollers, particular attention should be paid to preventing the roll core coated with adhesive against the inner wall of the mold, and affecting the bonding quality of the top roller. That is, no clay binder on the mold and no release agent on the roller core. The vulcanized rubber roller, to meet the requirements of strength, then the surface cutting and polishing machine finishing, to ensure that the roll surface roughness and roll shaft concentricity. (5) the basic requirement of CPU product mold: Material: the choice should be focused on: sufficient strength; sufficient heat resistance and dimensional stability; durability in line with service life; low manufacturing cost. When mass production, from the durability of commonly used metal materials, single or trial products, commonly used epoxy resin and other non-metallic mold, if the use of pressure die casting, the use of metal mold. The structure: in addition to ensure the size and shape of foreign products, should also pay attention to the pouring position, parting surface and exhaust, in order to achieve a,