铸铁零件焊接焊修技术探讨-焊接技术-中国焊接网 www_weld5_cn（Welding repair welding technology of cast iron parts - welding technology - China welding network www_weld5_cn）.docVIP

铸铁零件焊接焊修技术探讨-焊接技术-中国焊接网 www_weld5_cn（Welding repair welding technology of cast iron parts - welding technology - China welding network www_weld5_cn） Repair welding technology of cast iron parts: welding welding source network time: 2010-07-17 16:10 Click: 60 I want to contribute Abstract: This paper mainly introduces the welding characteristics of cast iron parts, cast iron welding quality improvement method is adopted according to these characteristics, should do the welding repair process of cast iron parts in the preparation and repair welding method, welding points, welding postprocessing is introduced. Key words: iron parts; welding method, welding repair, quality; The welding characteristics of 1 cast iron parts 1) easy to produce white. In the process of welding, welding and welding temperature zone part is very large, the welding heat by welding parts quickly to the outside, the welding pool by coagulation liquid to solid, if the cooling rate is too fast, especially near the fusion line, so that the graphite can precipitate, carbon and iron iron carbide are generated or a large part of the. This is silver white, so called white, the performance of hard brittle, difficult processing. 2) easy to crack. The weld is easy to produce white cast iron, cast iron cooling shrinkage than iron volume shrink almost twice as large, so in between near fusion line of white cast iron layer and the substrate without large shear stress, resulting in crack; welding and welding parts of the temperature difference is not large, welding the area of high temperature to the expansion, but it is part of the surrounding cold welding area to limit, instead of cooling shrinkage, cold metal around it and not let it pull the contraction, so the stress between them, tend to weld crack. If a white layer near the fusion line, will open a crack in the white layer. If the weld strength is higher than the matrix of cast iron, when the stress exceeds the ultimate strength of welding of cast iron