20 6 2010 6 Vol.20 No.6 The Chinese Journal of Nonferrous Metals June 2010 1004-0609(2010)06-1046-07 AM60 ( ) 1, 2 1 1, 2 1 1 (1. 730050 2. 730050) AM60 AM60 630 ~ 680 58.4~63.1 µm (Al Mn ) 8 5 AM60 TG249TG146.2 A Effect of pouring temperature on AM60 Mg alloy semi-solid slurry prepared by self-inoculation method ( ) 1, 2 1 1, 2 1 1 LI Yuan-dong , YANG Jian , MA Ying , QU Jun-feng , ZHANG Peng (1. State Key Laboratory of Gansu Advanced Non-ferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China; 2. Key Laboratory of Non-ferrous Metal Alloys and Processing, Ministry of Education, Lanzhou University of Technology, Lanzhou 730050, China) Abstract: The semi-solid slurry of AM60 Mg alloy was prepared by a novel self-inoculation method(SIM). The effect of pouring temperature on the semi-solid slurry prepared by self-inoculation method was investigated. The results show that the coarser dendrite reduces with the decrease of pouring temperature. A small block or rosette grain is obtained when the pouring temperature is near-liquidus. Meanwhile, the grain size also decreases, and it becomes approximately normally distributed. An ideal temperature process interval/window has to be required between 630 and 680 , and the grain size