【2017年整理】连续热镀锌板镀层细微缺陷及防范技术.pdfVIP

2010 年 6 月 武钢技术 Jun. 2010 # 5 4 # 第48卷 第 3 期 WISCO TECHNOLOGY Vol. 48 No. 3 (武钢研究院, 湖北 武汉 430080) : 主要介绍热镀锌钢板镀层表面存在的 如与钢基板、化学清洗、退火炉、锌液、气刀、平整等有 关的细微缺陷的产生原因, 同时还侧重介绍 如采用工艺手段、沉没辊辊面喷涂技术、沉没辊辊面涂层 封孔技术、流锌槽改善技术、锌液控制技术等, 以减少热镀锌钢板镀层表面细微缺陷和露钢缺陷。 : 热镀锌钢板;细微缺陷; 改善措施 : TG335.22 : B : 100824371( 2010)032 00542 04 Fine defect s on coatin g surface of con tinuous hot2dip galvan ized st eel sheet and it s pr even tive m easures ZHU Jiu2fa ( Researc and Development Center of WISCO, Wu an 430080, C ina) Ab st ract : T e present paper mainly introduces reasons of occurrence of t e fine defects on t e coating surface of ot2 dip galvanized steel s eets relative to t e substrate steel, c emical cleaning, continuous annealing furnace, zinc fluid, air knife, leveling and etc, and in t e meantime emp atically describes t e various tec nologies used, suc as t e process control tec nology, t e submersion roller surface spray coating tec nology, t e submersion roller surface coating to seal, t e ole tec nology, tec nology improvement of t e zinc troug and so on in order to reduce t ose fine defects and uncoated ar eas. Key wor ds: ot2dip galvanized s eet; fine defects; preventive measur es 近年来, 由于在热镀锌生产的各工序综合采 缺陷、划伤、冷轧中的表面损伤等。这些缺陷在钢 用了各种工艺控制措施, 锌和锌合金镀层钢板的 板和镀层界面引起Zn- Fe 合金爆发组织和不同 表面质量得到了很大改善。但是, 仍有一些难以 取向的锌枝晶。平整轧制以后, 由于光的反射差 鉴别和消除的细微缺陷存在, 这些缺陷常常逃过 异而使这些缺陷更加明显, 即使基板上一个很细 了严格的检验而送达最终用户。为了消除这些缺 小的疙瘩, 也会变得很突出, 很容易误判为锌渣。 陷, 最重要的是查明产生这些缺陷的源头。其中, 与钢基板有关的GA 镀层缺陷主要有: ¹基 来料基板质量差、不正确的基板清洗、热处理、热 板上的微小划伤造成的缺陷。基板划痕是钢板在 镀及平整工艺、搬运造成的表面损伤、用户加工操