酸解羧甲基复合变性淀粉浆料性能探究.docVIP

酸解羧甲基复合变性淀粉浆料性能探究 　　摘要：本文将木薯淀粉进行酸解和羧甲基化反应，制得了酸解羧甲基复合变性淀粉，对其进行了红外表征和浆液、浆膜性能的测试，并通过涤棉高支高密织物的上浆对比试验研究其实际浆纱织造效果。试验结果显示：酸解羧甲基复合变性淀粉属于高浓低粘浆料，粘度热稳定性好，浆膜性能均优于一般变性淀粉，对涤棉粘附性好，浆纱耐磨性、毛羽贴伏性好，织机效率、合格品率高，布品平整柔软，可以作为一种优良的涤棉高支高密织物浆纱材料。 关键词：酸解羧甲基复合变性淀粉；高支高密织物；浆纱质量；织机效率 中图分类号：TS103.864.1 文献标志码：B A Study on the Properties of Acidolysis Carbonxymethyl Composite Modified Starch Sizing Agent Abstract： In this paper， the acidolysis carboxymethyl composite modified starch was prepared by acidolysis and carboxymethylation reaction of cassava starch. Its structure was characterized by IR， the size property and sizing film property were tested and the practical sizing and weaving effect were studied through sizing contrast test on polyester/cotton high-count-density fabric. The test results show that the sizing agent has high concentration and low but thermal-stable viscosity， and the size film performance is better than conventional modified starch. It has good adhesion to polyester/cotton fabric， good sizing abrasion resistance and hairiness coverage as well as high loom efficiency and quality rate. Key words： acidolysis carboxymethyl composite modified starch； high-count-density fabric； sizing quality； loom efficiency 高支高密织物以其优良舒适的服用性能而深受消费者的青睐，市场销售十分走俏。但因其支数高、密度大、经纱细、紧度大等特点，浆纱的拉伸负荷、弯曲延伸耐磨性能要求较高，否则在织造中容易产生毛羽间相互纠缠，致使梭口不易开清、经纬线断头、绞头、吊经疵布、浆轴质量不过关等问题。目前在高支高密织物浆纱过程中，有以PVA与变性淀粉类混合为浆料，也有以组合变性淀粉类为浆料，但未见有酸解羧甲基复合变性淀粉应用于高支高密织物浆纱相关报道 。因此本文针对高支高密织物的特点，探讨将木薯淀粉进行酸解和羧甲基化复合反应成一种变性淀粉浆料，从试验和生产实践角度研究其对高支高密织物上浆性 能及效果。 1 试验部分 1.1 主要仪器和主要材料 主要仪器：MAGNA-IR550傅里叶红外光谱仪（Nicolet），Y991-6A电子织物强力仪，YG020型电子强力仪，Y391型纱线弹性仪，YG171B-2型毛羽测试仪，Y731型抱合力机，JJ-1电动搅拌器，YHW-1102型恒温烘箱，NDJ-79型回旋式粘度计，PHS-3C精密pH计。 主要材料：木薯淀粉，浓盐酸，乙醇（86%），氯乙酸，PVA1788（工业品），酸解淀粉（工业品），丙烯酸甲酯接枝淀粉（工业品），13 tex 65/35 T/C粗纱，14.5 tex纯棉粗纱，磷酸酯淀粉（工业品）。 1.2 酸解醚化复合变性淀粉浆料的制备 取一定量的木薯淀粉，用水配制成40%的淀粉乳，升温至38 ℃，加入淀粉质量13.5%的10 mol/L盐酸，恒温酸解3.5 h。反应结束后，离心脱水，加水配制成50% ～ 60%的淀粉乳，然后用 5 mol/L碳酸钠溶液中和至pH值 = 6，离心脱水，加水洗去中和产生的盐，洗至流出液无咸味为止，离心脱水烘干得酸变性淀粉成品。将酸变