大型储罐的应力腐蚀开裂.docx

2009年6月第 38卷 增刊施 工 技 术CONSTRUCT ION TECHNOLOGY543大型储罐的应力腐蚀开裂刘涛,沈士明(南京工业大学 ,江苏南京210009)[摘要 ]随着我国石油战略储备计划的实施 ,高硫原油的大型储罐建设成为必然趋势,大型原油储罐应力腐蚀开裂 的危害性也越来越大 。介绍对大型原油储罐应力腐蚀开裂研究的必要性 ,简述了应力腐蚀机理,重点介绍大型储 罐应力腐蚀开裂的影响因素与特征 。并提出相应的防护措施,指出大型储罐用高强钢的应力腐蚀试验及安全评 定 、寿命预测是该领域今后工作的一个重点 ,声发射在线检测技术是今后发展的方向。[关键词 ]应力腐蚀开裂 ;大型原油储罐 ;腐蚀环境;在线检测[中图分类号 ] TG174.41[文献标识码 ]A[文章编号 ] 100228498 ( 2009)S020543204Stress Corrosion Crack ing in Large2sca leTanksL iu Tao , Shen Sh iming(N anjing U niversity of Technology, N anjing, J iangsu 210009, China)Abstract:W ith the imp lementation of oil strategy reserve p rogram of China, the reserve of crude oil with high sulfur con2 tent becom es inevitable, and the stress corro sion cracking ( SCC) in large2scale crude oil tanks becomes a greaterdanger.In this paper the necessity for researching the SCC in large2scale crude oil tanks is introduced. and the mechanism of SCCis also exp lained.The emphasis is put on the introduction of the characters and influence factors of SCC in large2scale crudeoiltanks.Accordingtothese,someprotectionmeasuresforlarge2scalecrudeoiltanksareputforward.Accordingtothere2search status, it is p roposed that one research p riority of this field is the stress corrosion tests, safety assessm ent and lifep rediction for large2scale tanks, and on2line detection techno logy by acoustic em ission is the development direction.Key words: stress corrosion cracking; large2scale crude oil tank; corrosion environment; on2line detection我国石油消耗量以 4%的年增长率逐年增加,而国内原油量的产量增长率低于 1% ;因此国内石油生 产供应不足 ,原油进口量也越来越大,储运规模的增大使得储罐大型化的趋势成为必然 。同时,随着国家石 油战略储备计划的实施,鉴于建设储罐的经济成本以及我国在大型储罐设计 、施工上的技术突破,原油储罐 大型化已经成为趋势 ,今后几年,我国大型储罐的应用 将越来越广泛 [ 122 ]。世界原油的供应趋势是日趋劣质化 [ 326 ] 。2000年 的含硫原油 (硫含量 0. 5% ～2. 0% )和高含硫原油(硫 含量在 2%以上 )产量占世界原油总产量的 75%,其中硫含量在 1%以上的原油占世界原油总量的55%以上 ,硫含量在 2%以上的原油占 30%以上。而到2006 年为止,高含硫原油在世界原油总量中的比例已占到50%左右。可见世界原油的硫含量不断升高。原油供 应最集中的中东地区也以高硫原油为主。国际油价近 几年猛涨,且轻、重