高吸水性树脂对低水胶比混凝土性能影响.pdfVIP

学兔兔 2013年第7期 混凝土与水泥制 品 2013 No．7 7月 CHINA CONCRETE AND CEMENT PRODUCTS July 高吸水性树脂对低水胶比混凝土性能的影响 王立霞 (河南建筑职业技术学院，河南省建筑工程学校，郑州450064) 摘 要：利用高吸水性树脂(SAP)引入数量不等的内养护水，研究了低水胶比混凝土强度、重量损失、电阻率和 收缩的变化规律。结果表明，SAP的加入一定程度上降低了混凝土的抗压强度和劈裂抗拉强度．提高了混凝土的保 水性，混凝土表面和内部的电阻率也有所下降，混凝土的自收缩大大降低，且混凝土的早期干缩也有所下降。 关键词：混凝土；高吸水性树脂；强度；保水性；电阻率：收缩 Abstract：By adding super absorbing polymer(SAP)into the concrete with low water—binder ratio as an internal cur— ing agent，and by adding additional curing water to the concrete，the autogenous shrinkage of the concrete can be signifi． cantly reduced．The effects of the addition of SAP on the properties of the concrete with water-binder ratio 0．3 are investi— gated．The results show that the addition of SAP lcads to the decrease of the compressive and tensile strength and the electrical resistivity．The water retention for the concrete incorporation SAP is higher compared to the concrete without SAP．The addition of SAP into the concrete with lOW water—binder ratio can remarkably reduce the autogenous shrinkage． and it can also decrease the early dry shrinkage of concrete． Key words：Concrete；Super absorbing polymer；Strength；Water retention；Electrical resistivity；Shrinkage 中图分类号：TU528．1 文献标识码：A 文章编号：1000—4637(2013)07一O7—04 0 前言 水分的能力，有时吸收水的重量可以超过其自身重 低水胶比的高性能混凝土由于胶凝材料在水 量的500倍[6-7]。SAP与混凝土一起搅拌后，吸收部 化过程中产生相当大的化学收缩和自干燥．混凝土 分搅拌水。在胶凝材料水化期间，由于混凝土自干 硬化过程中会产生较大的自收缩变形。当混凝土的 燥．SAP逐渐释放其吸收的水分供胶凝材料进一步 自收缩变形受到约束时。就会在混凝土内部产生应 水化，降低混凝土自收缩。与LWA不同的是，SAP 力，而一旦内应力超过混凝土的抗拉强度，将导致 可以避免在混凝土中掺入力学性能较差的集料，提 混凝土早期开裂，继而严重地降低混凝土的耐久 高混凝土力学性能和均匀性嘲。 性。同时，由于低水胶比的高性能混凝土具