光引发剂对UV柔印油墨固化速度的影响研究.pdfVIP

编号：I20 光引发剂对UV柔印油墨固化速度的影响 魏先福，黄蓓青，张婉，张敬才 摘要：设计了UV柔印油墨的配方，选用了三种光引发剂制备油墨样品，测试了油墨样品 的固化速度。研究结果表明，不同的光引发剂及其用量对油墨固化速度有较大影响，三种光 引发剂中，使用907制备的油墨固化速度最快；采用配方实验的方法研究了复合光引发剂对 油墨固化速度的影响，测试结果显示其固化速度低于使用单一光引发剂907的固化速度。油 墨样品中引发剂907的含量为8%时固化速度最快。 关键词：UV柔印油墨；光引发剂；固化速率 中图分类号：TS202.3文献标示码：A 文章编号： WEI Xian-fu HUANG Bei-qing ZHANG Wan ZHANG Jing-cai Abstract: The formulation of UV Flexo Ink was designed, the inks were prepared by choosing three photoinitiators and the curing rates of inks were tested. The results show that different photoinitiators and its percentages significantly affect the curing rates of inks, and the curing rate of ink prepared by 907 is the fastest in three photoinitiators. The effect of co-photoinitiators on curing rate of ink is studied by the way of formulation experiment and the tested result indicates that the curing rates of co-photoinitiators are lower than the curing rate of photoinitiator907. The curing rate of the ink is the fastest of all, when the quantity of photoinitiator907 is 8%. Key words ：UV flexo ink; photoinitiator; curing rate 随着柔印以及UV固化技术的迅速发展，UV柔印油墨相比较于传统的水性和溶剂型柔印 [1] 油墨，在操作性、印刷品质、固化速度、环境保护等众多方面有着明显的优势 。固化速度 [2] 是UV油墨的一个重要性能，直接影响了UV柔印的印刷速度 。UV柔印油墨由UV单体(活 性稀释剂)、预聚物、光引发剂、颜料以及其它助剂组成，其中光引发剂对体系的固化速度 影响很大，它通过紫外光线的特定波长，激发并分解产生自由基，引发聚合反应，直接影响 [3] [4] 到预聚物和单体能否快速交联固化 。因此，选择合适的光引发剂是设计UV柔印油墨配 方的重要环节。 本论文通过选用五种光引发剂制备油墨，测试其固化速度，分别探讨光引发剂对UV柔 印油墨固化速度的影响，选用三种固化速度快的光引发剂进行复配，通过配方试验的方法确 定了复合光引发剂的最优比例；改变光引发剂的含量制备UV 柔印油墨，测试了油墨的固化 速度，可以得到最佳的光引发剂含量。 1实验 1.1原材料 研磨预聚物：丙烯酸酯类预聚物6311-100； 成膜预聚物：丙烯酸酯类预聚物6325-100，EB450； 单体：丙烯酸2-乙氧乙氧基乙酯 （EOEOEA）、新