超声在陶瓷膜处理乳化油废水中的应用研究 舒莉 邢卫红 徐南平∗ （南京工业大学膜科学技术研究所，江苏省材料化学工程重点实验室，江苏南京210009 ） 摘 要 本文考察了超声条件对陶瓷膜处理乳化含油废水效果的影响。结果表明：超声频率为21kHz、功率 为8w、超声源位置为膜管中部、超声发射方向与料液流动方向相同时，陶瓷膜处理乳化油废水的效果最好。 -2 -2 在此条件下，膜渗透通量从不加超声时的70L ·m ·h 提高为210L ·m ·h，且对油的截留率可达99.9％。 关键词 陶瓷膜 超声 含油废水 The influences of ultrasonic factors on processes of ceramic membrane using in wastewater Shu Li, Xing Weihong and Xu Nanping (Membrane Science Technology Research Center, Key Laboratory of Material-oriented Chemical Engineering of Jiangsu Province, Nanjing University of Technology, Nanjing 210009, China) Abstract The influences of ultrasonic factors on processes of ceramic membrane using in wastewater were investigated. The results showed that the permeation flux increased with adding ultrasound wave. When ultrasonic power is 8 watt, ultrasonic probe position is in middle of the membrane tube, and ultrasonic direction is the same as wastewater flow direction, the permeation -2 -2 flux increased from 70L·m ·h to 210L·m ·h, and the oil concentration of permeat is about 5mg/L. Keywords Ceramic membrane, ultrasound ，emulsion 引 言 在膜过滤过程中，由于存在浓差极化和膜污染等现象，导致渗透通量随运行时间的延长 而下降，这不仅影响了膜过滤的工作效率，而且缩短了膜的使用寿命。尤其是在污水处理过 程中，膜污染现象极为严重。为了减轻浓差极化和控制膜的污染，目前常用方法有增高流速 法、添加湍流促进器和反冲技术等[1] ，但这些方法均存在一些缺点，增高流速法和湍流促进 器功率消耗较大，并且湍流促进器会造成系统压力过大，而反冲法只对颗粒体系效果比较明 显。 近年来，超声波技术在废水处理方面的研究已经有了很大进展，由于超声波可以强化传 质，对于膜过程的强化，控制膜污染也有一定作用，因此本文将超声场作用引进陶瓷膜过滤 中，以期通过强化膜传质和延缓膜污染来实现高渗透通量和高分离因子的统一。 1 实验部分 1.1 实验装置 ∗通讯联系人：徐南平Tel.: 025 Fax: 025 Email: npxu@njut.edu.cn 基金项目：国家基础研究计划(No. 2003CB615702)，国家自然科学基金(NNSFC, No. [2] 本实验采用陶瓷微滤膜实验装置 ，膜管为氧化锆管式微滤膜，膜孔径为 0.2 μm ，膜 管内径7.5mm ，管长0.22m，有效膜面积0.0051m2 。 超声发生器和超声探头（换能器）为无锡南方声学电子有限公司制造，发生器功率为0～ 20w 可调，频率为 21kH