剑状微棒ZnO材料水热合成与气敏性能研究.docVIP

剑状微棒ZnO材料水热合成与气敏性能研究 　　摘要: 以氯化锌( ZnCl?2)和25%浓度氨水为原料, CTAB表面活性剂存在时，利用水热法制备了剑状微棒ZnO材料.采用X射线衍射仪和透射电镜等测试手段，对其物相和结构进行了表征.结果表明：此粉体材料结晶良好，直径小于??4?μm?，长度为??35?μm?.利用该材料制成气敏元件，并用静态配气法测试了元件的气敏性能.研究发现：元件在??200?℃??工作温度下，对丙酮气体有很好的灵敏度和选择性及较好的响应恢复特性.并对气敏机理进行了探讨. 　　? 　　关键词: ZnO；剑状微棒；水热法；气敏性能? 　　中图分类号:TN 304.92 文献标志码:A 文章编号:1672-8513(2011)05-0409-03 　　?? 　　Study on Preparation and Gas Sensing Property of? Sword-Like Microrod ZnO Material 　　 　　YANG Liu?fang?1，WANG Qing?hui?1，WANG Yu?de?2 　　? 　　 (1. Key Laboratory of Wireless Sensor Networks, Yunnan University of Nationalities, Kunming 650031, China;?2. Saba Transduction Technology Research Center, Yunnan University, Kunming 650091,China ) 　　 　　Abstract: Using zinc chloride solution and ammonia (25%) as raw materials, with the presence of surfactant (CTAB), the sword-like microrod ZnO material was synthesized by the hydrothermal method. The phase composition and microstructure of the prepared ZnO material were characterized with XRD and SEM. The results show that the ZnO material possesses a high degree of crystallization, its diameter below 4 μm. and its length about 30 μm. The gas sensing property of gas sensor fabricated with the prepared ZnO material was evaluated via the static volumetric method. At the operating temperature of 200 ℃, the gas sensor has high sensitivity and selectivity to CH?3COCH?3. The gas sensing characterization was also discussed. ? 　　Key words: ZnO; sword-like microrod; hydrothermal method; gas sensing property 　　 　　氧化锌(ZnO)是一种具有较宽带隙（?E??g=?3.37?eV?）的N型氧化物多功能半导体材料，具有气敏、压敏和光电等多种性能，一直受到人们的关注与重视［1］.ZnO的气体敏感性决定于它的晶粒大小、表面态和吸附氧的量等因素.ZnO纳米结构有着独特的优点，如大的比表面积、无毒、化学稳定、电化学活性以及高的电子传输特性等［2］.ZnO纳米结构可以吸附大量的气体，并且在吸附了气体之后形成特定的表面态，从而对其能带和导电性产生显著的影响.目前ZnO颗粒、ZnO线、ZnO带、ZnO棒等纳米材料的气敏性能已有研究报道［3-8］，对于多维纳米ZnO材料的气敏性能研究报道较少.作者采用水热法合成了剑状微棒ZnO材料，利用XRD、SEM等现代分析测试手段，对其物相、结构进行了表征，并将其作为气敏材料，制成烧结型旁热式气敏元件，测试了该气敏元件对NH?3、甲醛(CH?2O)、C?6H?5CH?3、CH?3COCH?3、C?2H?5OH 等的气敏性能. 　　 　　1 实验? 　　1.1 材料的制备? 　　剑状微棒ZnO材料采用水热法制备.将一定量的氯化锌以及CTAB