聚醚砜纤维载体染色性能研究.docVIP

聚醚砜纤维载体染色性能研究 　　文章采用Foron类分散染料对聚醚砜纤维进行载体染色，通过K/S值和染色牢度对染色效果进行评价。结果表明：载体Dilatin POE能明显提高聚醚砜纤维的可染性，随载体用量增加，纤维强力下降；载体Dilatin POE用量为 0.8 g/L，90 ℃染色45 min时，可达到较好的染色效果，断裂强力下降 10% 左右；染后聚醚砜纤维具有良好的耐洗和耐摩擦牢度。 　　In this paper, PES fiber was dyed in carrier dyeing process with Foron dyestuffs. The dyeing performance was evaluated by K/S value and colorfastness. The results showed that Dilatin POE can improve the dyeability of PES fiber consumedly, but the strength of the yarn decreased with the adding of the carrier. Dyeing at 90 ℃ for 45 minutes with 0.8 g/L carrier Dilatin POE has good dyeing effect on PES fiber and the breaking strength of the yarn decreasing about 10%. After dyeing, the colorfastness to washing and rubbing were good. 　　 　　聚醚砜（PES）树脂是一种综合性能优异的热塑性聚合物材料，它具有突出的阻燃性能，极限氧指数为38，具有自熄性；玻璃化转变温度为225℃，为无定形材料，连续使用温度为180～200℃。最初是作为阻燃性、耐热性、耐化学药品性和机械性能等方面都非常优异的特种工程塑料开发出来的，国内外极少见有真正在纤维方面进行应用开发的研究。北京服装学院采用熔融纺丝法制得了聚醚砜纤维，并应用于航空航天领域的先进复合材料，取得了较好的效果。 　　将聚醚砜纤维推广到民用纺织品，就要研究其染色性能。近年来对一些高性能纤维如芳砜纶、芳纶等大多采用载体染色法，以降低染色温度。考虑到聚醚砜的玻璃化转变温度也较高，且分子链上没有能与染料分子相结合的反应性基团，因此采用分散染料对其进行载体染色。 　　 　　1　试验 　　 　　1.1　材料与药品 　　聚醚砜纱线（35tex/24f，自制）；Foron艳红RD?CBR、Foron黄RD?C4GRL、Foron蓝RD?CE（Clariant（科莱恩）公司）；CTC?C480导染剂（北京中纺化工有限公司）；环保型载体DilatinPOE（Clariant公司）；磷酸二氢铵（A.R.）；洗涤剂；无水碳酸钠（A.R.）；皂粉。 　　 　　1.2　仪器 　　恒温水浴锅（余姚市东方电工仪器厂）、ORINTEX电子测色配色系统（意大利ORINTEX染色技术（北京）有限公司）、Y571A摩擦色牢度机（浙江温州纺织仪器厂）、SDLM228耐洗色牢度测试仪（美国SDLATLAS公司）、Q?CSUN氙灯实验箱（Q?CPANEL实验室产品公司）、Y172型纤维切片器（常州纺织仪器厂）、XPL?C1偏光显微镜（新天精密光学仪器厂）、YG021PC型电子单纱强力机（温州方圆仪器有限公司）。 　　 　　1.3　试验方法 　　（1）前处理 　　冷水洗→洗涤剂洗涤（洗涤剂4g/L，60℃×10min，浴比：1∶50）→热水洗（60℃×10min）→冷水洗→晾干。 　　（2）染色工艺 　　染色处方： 　　 　　染色工艺曲线： 　　 　　 　　1.4　测试方法 　　（1）K/S值 　　将染色纱线缠绕在硬纸板上，紧密排列，用ORINTEX电子测色配色系统测定样品的K/S值，测5次，取平均值。 　　（2）拉伸性能 　　单根纱线的断裂强力和断裂伸长率，按GB/T3916―1997，在YG021PC型电子单纱强力机上测定。隔离长度250mm，拉伸速度250mm/min，批次20次，取平均值。 　　（3）纤维染透性 　　用Y172型纤维切片器制取染色后纤维的横截面试样，在显微镜下观察试样的染透性。 　　（4）各项色牢度的测定 　　耐洗色牢度：参照GB/T3921.3―1997《纺织品色牢度试验耐洗色牢度：试验3》； 　　耐摩擦色牢度：参照GB/T3920―1997《纺织品色牢度试验耐摩擦色牢度》； 　　耐光色牢度：参照GB/T8427―1998《