C50机制砂高性能混凝土T梁张拉可靠性的研究.docVIP

C50机制砂高性能混凝土T梁张拉可靠性的研究 　　摘 要：采用同条件现场养生的试件对C50机制砂高性能混凝土T梁的7 d抗压强度和弹性模量进行大量的试验归纳总结，对T梁张拉后起拱度进行调查统计分析。研究结果表明：采用机制砂配制的C50高性能混凝土用于T梁施工，7 d强度大于45 MPa，弹性模量大于2.76×104 MPa，均能满足设计及规范要求；T梁7 d张拉后起拱度符合设计要求。 　　关键词：T梁；机制砂；高性能混凝土；弹性模量 　　中图分类号：U414.1 文献标志码：B 　　Research on Tension Reliability of C50 Tbeam with Highperformance Concrete of Manufactured Sand 　　LIU Baisheng 　　（Traffic Construction Project Supervision Consulting Company of Fujian Province， Fuzhou 350000， Fujian， China） 　　Abstract： A large number of tests on the 7day compressive strength and modulus of elasticity of C50 Tbeam with highperformance concrete of manufactured sand were conducted， and statistical analysis was carried out on the arch degrees of Tbeam after the tension. The results show that the 7day compressive strength of C50 Tbeam is higher than 45 MPa，and the modulus of elasticity is above 2.76×104 MPa. The two indicators meet the specification requirements， while the 7day arch degree of Tbeam after the tension meets the design requirements. 　　Key words： Tbeam； manufactured sand； highperformance concrete； modulus of elasticity 　　0 引 言 　　沈海复线高速公路莆田段A4全长6.5 km，混凝土工程量近25万m3，其中机制砂用量大约10万t，合同价5.0亿元。共有5座特大桥，T梁长度有25 m、30 m、40 m三种，共计1 225片。 　　公路桥涵施工技术规范（JTG/T F50―2011）要求后张法预应力筋的张拉和锚固应符合下列规定：张拉时结构或构件混凝土强度、弹性模量（或龄期）应符合设计规定；设计未规定，则混凝土强度应不低于设计强度等级的80%，弹性模量应不低于混凝土28 d弹性模量的80%[1]。 　　该工程设计文件要求：预制T梁预应力束必须待混凝土立方体强度达到混凝土强度设计等级的90%后，且混凝土龄期不小于10 d时，方可张拉，并及时压浆。 　　结合《机制砂在高性能混凝土中的应用》课题研究，对T梁的抗压强度和弹性模量进行大量的试验分析、归纳总结，合理给定混凝土预应力束的张拉龄期，以利于工程建设进度要求。 　　1 原材料检测及混凝土配合比设计 　　1.1 水泥 　　采用某品牌的P.O52.5水泥，其物理力学性能检测结果见表1。由表1可知：该水泥的物理力学性能符合要求。 　　1.2 粉煤灰、矿粉 　　采用某建材公司生产的Ⅰ级粉煤灰，矿粉使用S95矿粉，粉煤灰和矿粉的质量均符合试验要求。 　　1.3 细骨料 　　C50T梁高性能混凝土使用的细骨料为本标段破碎场的机制砂，其物理力学性能及颗粒分析试验 　　表1 某品牌P.O52.5水泥的物理力学性能 　　检测项目准稠度/%初凝时间/min终凝时间/min安定性比表面积/（m2?kg-1）抗压强度/MPa 　　3 d28 d28 d抗压强度富余系数/% 　　检测结果25.2185235合格34631.356.8108 　　规范要求≥45≤600合格≥300≥23.0≥52.5 　　结果见表2，颗粒级配曲线见图1。 　　1.4 粗骨料 　　C50 T梁高性能混凝土采用的粗骨料为本标段破碎场生产的4.75～19 mm二级配碎石，级配曲线见图2。 　　1.5 外加剂 　　C50 T梁高