掺杂锐钛矿相TiO2的第一性原理研究-材料物理与化学专业论文.docxVIP

摘 摘 要 摘 要 锐钛矿相 TiO2 由于具有许多良好的性能，如光催化性、超亲水性、抗菌性等，在 环境净化、太阳能电池和光电催化方面拥有广阔的应用前景，是一种优异的半导体光催 化剂。但是锐钛矿相 TiO2 禁带宽度较大，导致其对太阳光利用率很低，严重限制了其 广泛应用。研究表明，掺杂是一种有效的方法。本文采用计算机模拟计算，利用基于密 度泛函理论的第一性原理平面波超软赝势方法对 Bi、P、Hg 替位单掺杂 TiO2 和 Bi-N、 W-S、Fe-S、Mn-S 替位共掺杂锐钛矿相 TiO2 电子结构和光学性质进行了模拟计算，并 对结果进行了分析。 研究发现 Bi 掺杂锐钛矿相 TiO2 后，禁带中引入了杂质能级，禁带宽度略微变大， 在可见光区域吸收出现明显增强；P 掺杂锐钛矿相 TiO2 后，在禁带之内引入了孤立的杂 质能级，禁带宽度增大，并随着 P 掺杂浓度的提高而增大，吸收带边蓝移程度逐渐增大； Hg 掺杂锐钛矿相 TiO2 后，禁带中引入了杂质能级，Hg-TiO2 带隙增大，Hg/Ov-TiO2 带 隙减小，分别出现蓝移和红移。 研究发现 Bi-N 共掺杂锐钛矿相 TiO2 后，禁带宽度增大，禁带中出现了杂质能级， 在可见光区域吸收增强；W-S 共掺杂锐钛矿相 TiO2 后,在禁带中出现杂质能级，禁带宽 度的明显增大，吸收带边蓝移； Fe-S 共掺杂锐钛矿相 TiO2 后，禁带宽度变窄，禁带中 引入了杂质能级，吸收带边出现红移，可见光区域吸收明显增强；Mn-S 共掺杂锐钛矿 相 TiO2 后，禁带宽度略微变大，禁带中引入了两条杂质能带，在可见光区域出现明显 增强。 关键词：第一性原理;锐钛矿相 TiO2;替位掺杂;电子结构;光学性质 I Ab Abstract Abstract Anatase TiO2 which has broad application prospects in environmental purification, solar cells and photoelectric catalysis because of its excellent properties, such as photocatalysis, super hydrophilic, antibacterial, is an excellent semiconductor photocatalyst. Duo to the large band gap of anatase TiO2, which will lead to the low utilization rate of sun light, limits its application. Research shows that the doping is an effective method. In this paper, the electronic structures and optical properties of Bi, P, Hg for single doped and Bi-N, W-S, Fe-S, Mn-S for codoped anatase TiO2 were calculated using the first-principles plane-wave ultra-soft pseudo-potential method based on the density functional theory. It was found that the impurity levels in the band gap was introduced into Bi doped TiO2, the band gap increased a little, and the doping induce significantly enhancement in visible light. To P doped TiO2, the isolated impurity levels appeared in the band gap, and the width of forbidden band, absorption enhancement in the visible region and the blue shift degree of absorption spectral edges increase with P doping concentration increasing. The band gap of the Hg-doped anatase TiO2 without O vacancy is narrowed, while