锆合金力学性能剖析.docVIP

锆合金力学性能剖析 　　【摘 要】本文主要通过分析Zr-4合金材料的室温拉伸性能和高温拉伸试验特点，提出利用金属材料 拉伸试验方法测量Zr-4合金室温、高温拉伸性能。并通过比较分析锆合金管材在不同温度和应力下的高温拉伸性能试验数据及室温拉伸性能数据，结果表明试验所用Zr-4合金拉伸性能数据集中，误差较小。 　　【关键次】高温拉伸性能；室温拉伸性能；拉伸试验；应力；应变 　　中图分类号： TG146.414 文献标识码： A 文章编号： 2095-2457（2017）35-0039-002 　　Zirconium alloy mechanical properties analysis 　　DOU Li-juan XU Cheng TANG Ying SUN Li-yuan 　　（State Key Lab of Nuclear Grade Zirconium， Key Laboratory of Nuclear Grade Zirconium of National Energy Nuclear Grade R D Center， Baoji Shaanxi 721013， China） 　　【Abstract】In this paper， the tensile properties of Zr-4 alloy at room temperature and high temperature were investigated by tensile test of Zr-4 alloy at room temperature and high temperature. By comparing and analyzing the tensile test data and the tensile test data at different temperatures and stresses， the results show that the data of the tensile properties of the Zr-4 alloy used in the experiment are less concentrated. 　　【Key words】High temperature tensile properties； Tensile properties at room temperature； Tensile test； Stress； Strain 　　0 前言 　　拉伸?验是材料力学性能测试中最常见试验方法之一。试验中的弹性变形、塑性变形、断裂等各阶段真实反映了材料抵抗外力作用的全过程，它具有简单易行、试样制备方便等特点。拉伸试验所得到的材料强度和塑性性能数据，对于设计和选材、新材料的研制、材料的采购和验收、产品的质量控制以及设备的安全和评估都有很重要的应用价值和参考价值。锆合金室温拉伸性能表示锆合金材料在10℃～35℃温度范围内的拉伸试验结果，对于温度要求严格的试验，温度范围应控制在23℃±5℃条件下进行。锆合金的高温拉伸性能则表示锆合金材料在温度大于35℃条件下的拉伸试验结果。由拉伸试验所得到的应力-应变曲线图给出了材料的强度性能和塑性性能指标，它是塑性成形力学理论最基本的试验资料。原子间结合力的程度，实际反应了在屈服条件以下材料抵抗变形的能力，在工程应用上有重要的作用。本文对我公司常进行的包壳管和连接棒室温、高温拉伸性能进行比较分析、探讨、总结，得出结论。 　　1 试验原理及方法过程 　　1.1 试验原理 　　（1）材料的拉伸性能主要与材料内部的成分和组织结构有关，同时还受到加载速度、温度、受力状态等因素的影响。一般金属材料按其塑性变形性能的不同可分为：有明显屈服流动台阶和无明显屈服流动台阶两类。而我们常用的有色金属锆则属于后者，对于此类金属材料规定有0.2%残余应变时的应力作为条件屈服强度Rp0.2，或者把割线模量Es=0.7E的应力作为抗拉强度Rm（E为弹性模量） 　　（2）拉伸图与应力―应变图，试验时，将试样安装在万能试验机上，然后均匀缓慢地加载，使试样拉伸直至断裂。绘出试样在试验的过程中工作段的伸长与受力的关系曲线，即F-Δl曲线，称为拉伸图。 　　屈服极限Rp0.2及抗拉强度Rm是特性点的应力，均是反映材料力学性质的重要指标，而延伸率 　　A则是反映材料塑性性质的重要指标。 　　1.2 试验控制及试验数据 　　1.2.1 试验控制 　　试验选择CMT5105拉伸试验机，试验机的测力系统按照GB/T16825.1进行校准，其准确度优于0.5级。引伸计的准确度级别符合GB/T12160的要求，不劣于1级准确度。计算机控制拉伸试验机满足满足GB/T2206