钢铁材料保护层法防腐技术研究进展1.pdf

2015 （第十九届）冶金反应工程学术会议集 钢铁材料保护层法防腐技术研究进展1 王蓝卿, 李 慧, 梁精龙 （华北理工大学冶金与能源学院现代冶金技术教育部重点实验室唐山 063009 ） 摘 要：随着钢铁产量的增加，每年因钢铁腐蚀造成的损失也是相当巨大，钢铁防腐对减少钢铁腐蚀损失有重要的意义。又由 于近年来国家对环保力度的加大以及现在应用最广泛的方法就是形成防腐保护层法，环境友好型的钢铁外加保护层防腐技术成为 了未来的发展方向，本文重点介绍水溶性有机富锌底漆和钢材表面硅烷处理两种环保钢铁表面防腐技术。 关键词：钢铁腐蚀；防腐保护层法；环保 中图分类号：TG146.1 The Research Progress of Anticorrosive Technology of Pro-tecting-layer of Iron Steel Material Wang Lan-qing, Li Hui （Key Laboratory of Ministry of Education for Modern Metallurgy Technology, College of Metallurgy and Energy, North China University of science and technology, Tangshan 063009, China） Abstract ：with the increase of steel production, the loss caused by steel corrosion every year is also very great. And because in recent years countries on environmental protection increased and is now the most widely used method is the formation of corrosion protection coating method, the environment friendly steel external protection coating technology has become the development direction in the future. This paper focuses on the water solubility of organic zinc rich primer and steel surface with silane treatment two environmentally friendly steel surface anti-corrosion technology. Key words ：Steel corrosion; corrosion protection layer method; environmental protection 目前中国钢铁产量位居世界第一位，每年因钢铁腐蚀造成的钢铁消耗相当于当年钢铁产量的10%-20% 。因 钢铁腐蚀带来的直接经济损失约占生产总值的 6%左右。钢铁腐蚀所带来的不仅仅是巨大的经济损失，同时， 常用的钢铁器件的腐蚀具有高度的安全隐患，可能造成非常严重的安全事故，造成不可估计的财产损失和人身 伤害[1-3] 。金属的锈蚀是金属表面最常见的腐蚀形态。金属材料受到周围介质的作用而遭到破坏，这种腐蚀过程 一般通过化学腐蚀和电化学腐蚀两种途径进行。金属锈蚀给人类造成极大的危害。我国每年因金属锈蚀造成的 损失可达千亿以上。金属腐蚀事故引起的停产、停电等间接经济损失就更无法估计。因此，研究和分析金属的 腐蚀防护方法来控制和减少金属的腐蚀，对减少安全事故、财产损失和国民经济发展意义十分重大[4,5] 。 1 金属腐蚀种类 化学腐蚀：化学腐蚀是金属材料与干燥的、并且能与之发生化学反应的气体或者与能非电解质溶液发生化 学反应，只是发生氧化还原反应。这种化学腐蚀只有在特定的环境下才会发生。 电化学腐蚀：电化学