灰铸铁激光表面熔化处理的表面质量分析.pdfVIP

命 ~(I 龙 第 13 卷 ;在 12 期 灰铸铁激光表面熔化处理 的表面质量分析 谢淑明 刘海珍 陈兰英 (上海第二工业大学) (中国科学院上海尤机所〉 提要:探讨了灰铸铁激光表面熔化处理表面的质量。试验表明:通过调节激光 器的输 出功率、光斑直径和扫描速度可以方便地控制熔化层深度和表面平整度。采 用惰性气体保护可以基本消除表面气孔。适当的选材与低温预热及后热可以抑制表 面裂纹的产生。 Analysis of surface quality of grey iron subjected to laser melting treatment Xie Shuming, Liu Hαizhen (Shanghai Second Polytechnic Un iversity) ChenLαnying (Shanghai Institute of Optics and Fine Mechanics , Academia Si口ica) Abstract : This paper deals with the infiuence of laser beam on th e wídth and depth of melting zone and surface smoothness . The exp erímen tal !.esult shows that the depth of h ardened zone and smoothness of surface can be contr olled conveniently by var ying th e power output beam diameter and scanníng rate of laser light. By mean司 of shielding gases p orosity can be reduced gr回tly . Proper selection of materials, preh eating- and PRstheating can h elp to avoid cracking. 重的质量问题:①熔凝带表面有凹凸不平的 波纹;②熔凝区表面及内部存在有气孔;③ 引 熔凝区表面及内部存在有宏观和微观裂纹。 灰铸铁经激光表面熔化处理后能获得机 后面两点破坏了熔凝带的连续性，影响了表 械性能优良的熔凝带p 熔区硬度::::;H 900，耐 面的美观p 且对承受冲击或接触应力高的零 m 磨性可与气体氧化比拟，因此引起了国内外 件产生不良后果。 本文对激光表面熔化处理后的表面平整 热处理工作者的广泛兴趣。 收稿日期: 1985 年8 月 22 日. 但是铸铁经激光熔化处理后表面存在严