复合薄膜的制备及性能.docxVIP

AbstractTi02 Abstract Ti02 films were cheap，non-toxic，stable，easily to use and had the advantages of recycling．It had a very wide range of application in the field of environmental pollution control and photoelectric conversion．At present，Ti02 films have entered a practical stage， but there are still many technical problems of low photocatalytic activity and low utilization of sunlight and Ti02 films photoelectric conversion technology is still in the experimental stage．In recent years，technology of Ti02 films has a rapid development，including precious metals deposition，transition metal ion dopin易the non-metallic doped photosensitive surface and the methods of compound semiconductor．In this paper,the new material Multi-walled carbon nanotubes(MWNTs)was added to Ti02 and it was successful to prepare a MWNTs／Ti02 composite film of stability and good translucent．In this Paper,the photoelectric conversion film composite nature and the nature of photocatalytic activity etc were studied． Firstly,Ti02 nanoparticles colloidal solution Was synthesised by sol——gel and while MWNTs Was scattered in sodium dodecyl sulfate(SDS)forming aqueous solution in ultrasound uniform suspension．Czochralski method Was used in the dipping MWNTs films and Ti02 films on the conductive glass and slide film and after a series of treatment MWNTs／Ti02 composite film was maded． Secondly,the nature of photovoltaic conversion of MWNTs／Ti02 composite film Was studied through electrochemical method．It Was found that in compared to Ti02 film， MWNTs／Ti02 films had a higher voltages，stronger photocurrent．Alkaline electrolyte had a greater impact on the composite film photocurrent．Neutral electrolyte had a greater impact on the films voltage and had a response to visible light．It Was told that after the addition of MWNTs，the nature of Ti02 Was optimized． Thirdly，the photocatalytic nature was studied on the composite film of the substrate to slide for the Ti02 and MWNTs／Ti02 films．It wad showed that aRer add