7m 焦炉焦炭热强度研究1 张文成 任学延 王春花 （上海梅山钢铁股份有限公司，南京 210039 ） 摘 要 针对 7m 焦炉焦炭进行质量特性分析，探讨了焦炉炉型对焦炭质量的影响，结果显示，7m 焦炉焦炭比 6m 焦炉焦炭的日本转鼓强度 DI （150/15)和焦炭热强度（CSR ）均有所提高；探讨了影响焦炭热强度的关键因素， 结果表明，炼焦煤的粘结性和变质程度是对焦炭热强度的关键影响因素，优化的配煤结构、配煤细度和结焦时间 也是获得高质量焦炭的保证。 关键词 焦炉 焦炭 热强度 Study on Thermal Strength of Coke of 7m Coke Oven Zhang Wencheng Ren Xueyan Wang Chunhua (Shanghai Meishan Iron Steel Co., Nanjing, 210039) Abstract The cokes quality of 7m coke oven was analysed by discussed the type of coke oven and the key factor of coke Thermal Strength. The results show that the DI(15/150) and the CSR was advanced than 6m coke ovens, and that cohere properties of the coking coal and petrology components are important factors to thermal properties of coke. The structure of coal blending, the smashed degree and the time of coking was optimized is important to obtain high quality coke. Key words coke oven, coke, thermal strength 1 引言 [1] 随着高炉大型化及喷煤量的增加，焦炭热强度逐渐成为考核冶金焦炭质量的主要指标之一 。梅钢 4 号高炉（容积 3200m3 ）投产，与此相适应，2 ×60 孔 JNX3-70-1 型 7m 焦炉及 190t/h 的干熄焦装置于相继 投产，对焦炭质量特别是焦炭热强度产生了一定的影响。7m 焦炉作为新的炉型，对焦炭质量及炼焦工艺 产生怎样的影响，本文从对热强度影响的角度进行分析讨论。 2 试验方法 2.1 试验装置 焦炭反应性试验装置是北科大自发研制的，该装置的一个突出特点是增加了失重分析仪，能将 2h 内 失去的焦炭质量以图表和数据的形式传送到计算机上，根据此数据计算反应性 CRI，能避免将升温和降温 过程中焦炭的损失量带入反应性的计算中，减小试验误差。根据标准 GB/T4000—2008 《焦炭反应性及反 应后强度试验方法》。 张文成(1972-)，男，硕士，高级工程师，从事配煤炼焦研究工作，njmsjszx@ 8-170 第八届（2011 ）中国钢铁年会论文集 2.2 试验样品 试验样品为 2010 年度梅钢 7m 焦炉和 6m 焦炉的焦炭。 2.3 试验方法 除进行焦炭热强度进行分析外，同时对配套的配煤质量进行分析，炼焦煤的分析参照对应国标进行。 3 试验结果与讨论 3.1 焦炭热强度总体趋势 对全年焦炭热强度进行分析，对 7m 焦炉的焦炭热强度随时间进行分析，如图 1 所示。 图 1 焦炭 CSR 随时间分布图 图2 7m 焦炉和 6m 焦炉焦炭 CSR 对