400+MPa超级钢热连轧过程中再结晶及流变应力的预测.pdfVIP

年 月 2002 6 钢 铁 研 究 第 期（总第 期） 3 126 June 2002 （ ） Research on Iron SteeI No . 3 Sum126 400 Mpa 超级钢热连轧过程中再结晶 及流变应力的预测! 许云波 刘相华 王国栋 （东北大学） 摘 要 开发了描述低碳钢软化行为的再结晶模型，并对奥氏体再结晶动力学和 微观组织演变进行了模拟计算。在此基础上建立了计算精轧过程应力—应变模型，根 据现场数据预测了400 Mpa 级超级钢细晶化轧制的轧制力，预测结果与实测值吻合。这 项研究可广泛用于钢种开发、轧制规程设定和优化以及轧制过程的在线控制。 关键词 热轧 流变应力 再结晶动力学 微观组织演变 PREDICTION OF RECRYSTALLIZATION AND FLOW STRESS DURING MULTIPASS HOT ROLLING OF 400 MPa SUPER - STEEL Xu Yunbo Liu Xianghua Wang Guodong （ ） Northeastern University Synopsis A recrystaIIization kinetics modeI to describe the softening behavior of Iow carbon steeI was deveIoped and used for simuIation of austenite recrystaIIization and microstructure evoIu- tion . On this basis， a fIow stress modeI to caIcuIate the muItipass stress - strain curve during finish- ， ing roIIing was made out . By means of these modeIs and on - site data the predicted resuIts of roIIing road during finishing roIIing of 400 Mpa super - steeI were given and they were in good ac- cordance with measurements . It showed that these modeIs can be wideIy used for steeI grades de- sign， roIIing scheduIe optimization and on - Iine controI of hot roIIing pro