摘 要 论述了Mg-Al-Zn系合金经过固溶处理后组织和耐腐蚀性能的变化。通过观察经固溶处理后的组织及塔菲尔曲线，对Mg-Al-Zn系合金固溶处理后的组织和电化学腐蚀行为进行了研究。结果表明，经过固溶处理后的镁合金显微组织晶粒长大明显，β-（Mg17Al12）相部分溶解在基体组织中，在温度达到560度以上时，组织发生过烧现象。与未经处理镁合金的耐腐蚀性能相比，经过固溶处理后的镁合金耐腐蚀性能无明显增加。 关键词：镁合金；固溶处理；显微组织；耐腐蚀性能  Title: Solution Treatment on Mg-Al-Zn alloys organizations and the impact of corrosion resistance Abstract Discusses the Mg-Al-Zn alloy after solution treatment and corrosion resistance after the organization changes. By observing the organization after solution treatment and the Tafel curves of Mg-Al-Zn alloy after solution treatment and electrochemical corrosion behavior was studied. The results showed that, after the magnesium alloy after solution treatment microstructure grain growth significantly, β-(Mg17Al12) phase partially dissolved in the matrix organization, in the temperature reaches 560 degrees, the tissue over-burning phenomenon. With untreated corrosion resistance of magnesium alloys compared to that after the magnesium alloy after solution treatment did not increase the corrosion resistance. Keywords： Magnesium alloy；Microstructure；Corrosion resistance  学位论文原创性声明 本人郑重声明：所呈交的论文是本人在导师的指导下独立进行研究所取得的研究成果。除了文中特别加以标注引用的内容外，本论文不包含任何其他个人或集体已经发表或撰写的成果作品。对本文的研究做出重要贡献的个人和集体，均已在文中以明确方式标明。本人完全意识到本声明的法律后果由本人承担。 作者签名： 日期： 年 月 日 学位论文版权使用授权书 本学位论文作者完全了解学校有关保留、使用学位论文的规定，同意学校保留并向国家有关部门或机构送交论文的复印件和电子版，允许论文被查阅和借阅。本人授权　　 　 　大学可以将本学位论文的全部或部分内容编入有关数据库进行检索，可以采用影印、缩印或扫描等复制手段保存和汇编本学位论文。 涉密论文按学校规定处理。 作者签名： 日期： 年 月 日 导师签名： 日期： 年 月 日 目录 目录 3 第一章 绪论 4 1.1 选题的目的与意义 4 1.2 镁合金 5 1.2.1 镁合金的发展 5 1.2.2 镁合金的性能及应用 6 1.2.2.1 镁合金在汽车上的应用： 6 1.2.2.2 镁合金在3C产品上的应用： 7 1.2.3 镁合金的种类及发展趋势 7 1.2.3.1 镁合金的种类 7 1.2.3.2 镁合金的发展趋势 8 1.3 合金元素对镁合金组织和力学性能的影响 10 1.3.1 镁合金主要化学成分 10 1.3.2 合金元素对合金组织和力学性能的影响 11 1.4 固溶处理的作用 13 1.4.1 固溶与时效处理 13 1.5 稀土镁合金 14 1.5.1 稀土镁合金的发展现状 14 1.5.2 稀土镁合金的开发应用及前景 15 1.6 本论文的主要研究内容 16 第二章 试验方法及设备 17 2.1 实验选用材料 17 2.1.1 固溶处理实验所使用的材料 17 2.1.2 金相实验选用的材料 17 2.1.3 耐腐蚀实验所使用的材料 17 2.1.4 X射线衍射实验所使用的材料 17 2.2 实验方案 17 2