连铸结晶器异形足辊.docVIP

连铸结晶器异形足辊 杜松林 　　摘　要　提出了一种不同于连铸结晶器常规圆柱形足辊的异形足辊。这种足辊的特点是中心部位凸出，能有效地压缩出结晶器下口的坯壳，从而减轻铸坯鼓肚量，防止铸坯角部纵裂纹及由此引发的漏钢事故，经马钢三钢厂板坯和方坯连铸机实际应用，效果良好。使板坯角部纵裂漏由投产初期的0.73%下降为0。　　关键词　连铸机结晶器　足辊　异形足辊 Profiled Foot Rolls of CC Mould Du Songlin(Ma Anshan Iron Steel Co. Ltd) Abstract　This paper introduces the profiled foot rolls of CC mould different from common cylindrical foot rolls. It is characterized by protruding in central part through which the shells can be compressed out of the lower gate of the mould and therefore reduce the buldging on cast slabs. Longitudinal corner cracks on slabs can be prevented so as to avoid breakout. Acconding to the application in slab and billet continuous casting machine in No.3 Steelmaking Plant at Ma Anshan Iron Steel Co. Ltd, the results are satisfactory, and the longitudinal corner cracks reduces from 0.73% in initial production process to 0.Keywords　CC mould　foot roll　profiled foot roll 1　前言 　　结晶器作为连铸机的心脏，是提高铸机主产率和铸坯质量的关键部件。对于结晶器的几何尺寸、支撑方式等方面的研究，许多文献做过报道。但足辊的形状及间隙的调整对铸坯质量的影响却未见报道，事实上足辊的形状及其调整对铸坯的角部纵裂漏钢有显著的影响。结晶器足辊通常是圆柱形，足辊与锥度线留有一定间隙，对铸坯起支撑和导向作用。文中提出异形足辊及足辊对铸坯的压缩概念，以减少铸坯的角部纵裂纹及由此引发的角部纵裂漏钢事故。马钢三钢厂在140mm方坯和板坯上实际使用这种足辊效果显著。使马钢三钢厂板坯连铸的角部纵裂漏钢率由投产初期的0.73%下降为0。异形足辊技术1996年获国家专利。 2　铸坯角部纵裂及其漏钢产生的原因 　　无论是方坯还是板坯，在浇铸过程中都会发生角部附近的裂纹，严重时产生漏钢。这是一种由于铸坯从内部撕裂造成的漏钢事故，其产生的原因有两个方面。2.1　凝固坯壳的不均匀性　　对出结晶器下口的坯壳解剖发现，在角部附近出现一个凝固壳最薄弱区域。严重时该处坯壳的厚度甚至只有中心部位的1/2，见图1和图2。对于马钢三钢厂的板坯凝固坯壳而言，角部距离宽面中心200mm以内的坯壳由薄逐渐变厚，角部到窄向中心同样有一个由薄变厚的过度区。这样在角部10～30mm以内形成坯壳最薄区域，这也是角部纵裂漏钢的发生之处。 图1　板坯凝固坯壳的厚度不均匀状况(220mm×1000mm×1/2) 图2　90mm×90mm方坯凝固坯壳厚度不均匀状况 2.2　铸坯的鼓肚　　铸坯坯壳形成之后，在钢水静压力的作用下，必然会产生鼓肚。若不加以限制，当鼓肚量超过某一临界值时，就可能把坯壳撕裂，直至发生漏钢。合适的结晶器锥度对结晶器内凝固坯壳的鼓肚能进行有效的限制，但是出结晶器下口之后，坯壳仍然会鼓肚，这时只有通过足辊起作用，达到这一目的。如果足辊形状不合理，调整不当，就有可能发生角部纵裂漏钢。马钢三钢厂板坯发生角部纵裂漏钢前铸坯窄面的鼓肚量见表1。 表1　角部纵裂漏钢的铸坯鼓肚情况 炉　　号 1-2810 1-6430 2-2021 鼓肚量/mm 8 9 7 炉　　号 2-3103 2-5151 3-446 3-3630 鼓肚量/mm 9.5 11.5 11 6 　　因此在钢水静压力的作用下坯壳的鼓肚，将最薄弱的角部坯壳撕裂，轻则成为角部纵裂纹，重则发生漏钢事故。 3　异形足辊及足辊的压缩调整 　　从前面的讨论可知，在目前所使用的结晶器条件下无论方坯还是板坯，由于凝固坯壳的不均匀性，在角部附近都会形成一个最薄弱区域。在钢水静压