《扩展组合模连续铸挤铝管材的挤压力分析（英文版）》.pdfVIP

Trans. Nonferrous Met. Soc. China 24(2014) 3621−3631 Extrusion force analysis of aluminum pipe fabricated by CASTEX using expansion combination die 1 1 1 2 3 1 Fu-rong CAO , Jing-lin WEN , Hua DING , Zhao-dong WANG , Chuan-ping YU , Fei XIA 1. School of Materials and Metallurgy, Northeastern University, Shenyang 110819, China; 2. State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China; 3. Dandong Feituo Aluminum Products Co., Ltd., Dandong 118000, China Received 24 November 2013; accepted 14 April 2014 Abstract: To determine the extrusion force of pipe fabricated by continuous casting and extrusion (CASTEX) using an expansion combination die, the metallic expansion combination die was divided into diversion zone, expansion zone, flow dividing zone, welding chamber, and sizing zone, and the corresponding stress formulae in various zones were established using the slab method. The deformation zones of CASTEX groove were divided into liquid and semisolid zone, solid primary gripping zone, and solid gripping zone, and the formulae of pipe extrusion forces were established. Experiments were carried out on the self-designed CASTEX machine to obtain the aluminum pipe and measure its extrusion force using the expansion combination die. The experimental results of radial extrusion force for aluminum pipe are in good agreement with the calculated ones. Key words: continuous casting and extrusion; continuous extrusion; expansion combination d