不同处理方式对羊毛织物风格的影响 周爱晖 （福建省纤维检验所，福建 福州 350026） 摘要：采用KES-FB 织物风格仪，探讨了经不同预处理工艺对毛织物风格的影响。结果表明：羊毛经蛋白酶处理或H2O2/DCCA＋酶两步法处理后柔软感均上升，但弹性回复能力、蓬松感都下降。单独酶处理后表面粗糙度下降；H2O2＋酶两步法处理样的表面粗糙度上升；DCCA＋酶两步法处理样的表面粗糙度较单独酶处理样进一步降低。 关键词：羊毛织物；H2O2；DCCA；蛋白酶；织物风格 中图分类号：TS195. 56 文献标识码：A The effects of different treatment on the fabric style of wool ZHOU Ai-hui (Fujian Provincial Fiber Inspection Institute Fuzhou, Fujian, 350026, China) Abstract : H2O2、DCCA were used as pretreatment agents to study the effects on fabric style of wool fabric treated by proteases. The results showed that, the wool fabrics were treated by protease or H2O2/DCCA+protease two-step procedures, the softness performance was increased, but the elongation recovery ability and the bulkiness property of the wool fabric were decreased. The surface roughness, which was treated by single protease, was decreased. however, the surface roughness was raised by H2O2+protease two-step procedures. Meanwhile, after DCCA+protease two-steps procedures treatment, the surface roughness was lower than single protease treatment. Key words : wool fabric; H2O2; DCCA; protease; fabric style 近年来，羊毛织物向内衣化和轻薄型的方向发展，人们对羊毛织物服用与护理的要求也越来越高，如要求羊毛服装可以“机可洗”，服用或洗涤后可以抗皱或免烫，手感柔软以及可以抗起毛起球等等。实际上，羊毛织物要实现以上这些功能的处理并不是完全独立的，而是相辅相成、密切相关的，其中最为基本的任务就是要解决好羊毛织物的防毡缩问题。传统的羊毛防毡缩大都采用氯化- Hercosett工艺，国内外很多学者出于对环保的考虑，多选用H2O2作为预处理剂，辅以蛋白酶处理进行羊毛织物的防毡缩加工[1]。不同防毡缩处理方式对羊毛处理后的织物风格具有不同的影响 织物风格是一种感觉效应，综合反映织物外观、舒适性及美感[2]。为考察不同处理方式对羊毛织物风格的影响，本文选用KES系统分别测定用于评定手感风格的14个物理量，主要包含织物的拉伸特性、剪切特性、弯曲特性、压缩特性和表面特性，其各指标的特征含义及风格含义如表1[3]所示。 作者简介：周爱晖（1984 -），女，主要从事纺织品检验工作，E-mail: wx_zah@163.com。 表1 KES织物客观力学物理性能指标体系表 Tab.1 Index system of objective physical mechanical properfies of fabric (KES) 力学性能 指标 特征值含义 单位 风格含义 说明 拉伸特性 LT WT RT 拉伸线性度 拉伸比功 拉伸功回复率 — N.cm/cm2 % 柔软感 变形抵抗能力 变形回弹性 WT越大，织物越坚牢，不易变形 RT越大，织物弹性越好 剪切特性 G 2HG 2HG5 剪切刚度 剪切滞后矩（=0.5o） 剪切滞后力（=5o） N/cm,deg N/cm N/cm 变形抵抗能力 回复能力 回复能力 2HG其值越小，回复能力越好，反之差 2HG5其值越小，回复能力越小，反之差 纯弯曲特性 B 2HB 弯曲刚度 弯曲滞后矩 N.cm2/cm N