CAB-381-20BP介绍.ppt

FORMULATING ALCOHOL RESISTANT PLASTIC COATINGS WITH EASTMAN CELLULOSE ESTERSEASTMAN CAB 用于耐醇性塑料涂料配方 Criteria to formulate a good alcohol resistance coating制定一個好的耐醇配方的標准 Thermoplastic acrylics should have high Tg and good alcohol resistance 需要高玻璃化溫度和耐醇性好的熱塑性丙稀酸樹脂 Resins (including CAB) system should not contain any free hydroxyl groups 樹脂体系（包括CAB）不能含有游离羻基 Higher molecular weights material usually gives better alcohol resistance 分子量高的材料通常可提供好的耐醇性 Eastman CAB 381-20BP Product Introduction 產品介绍 CAB 381-20BPTypical Properties*典型性能 Butyryl content = 36 丁基含量= 36 Acetyl content = 15.5 乙基含量= 15.5 Hydroxyl content = 0.8 羻基含量= 0.8 Melting range, oC = 365 - 383 熔融范围， oC = 365 - 383 Tg, oC = 128 玻璃化溫度， oC = 128 Molecular weight, Mn = 83,000 分子量， Mn = 83,000 Testing of CAB 381-20BP CAB 381-20BP的測试 Evaluated for viscosity, DFT, appearance, double ethanol rubs, ethanol spot test, cross-hatch adhesion, pencil hardness and tape pull-off 測試粘度，干膜厚度，外观，酒精循環擦拭，酒精沾污測试，交叉划格法測試附著力，鉛筆硬度和透明拉拔 Tested with six thermoplastic acrylics, Paraloid B66, Paraloid A21, Neocryl B805, Degalan M825, Degalan LP68/04 and Degalan M890 共測試六种熱塑性丙稀酸樹脂：Paraloid B66, Paraloid A21, Neocryl B805, Degalan M825, Degalan LP68/04 and Degalan M890 Ratio of Acrylic:CAB (on solids basis) = 4:1 丙稀酸樹脂:CAB（固体份比） = 4:1 Coated samples flashed off for 20 minutes, baked for 15 minutes @ 70oC and aged for 24 hours before testing 被噴涂的樣品在空气中放置20 分钟， 然后放入70oC烘箱中烘烤15分钟，取出放置于常溫中24小時后測試 Conclusions　結論 CAB 381-20BP improves the metallic appearance of the coating CAB 381-20BP可提高含金屬粉涂料涂膜的外观 Alcohol resistance of all the coatings were not affected by the addition of CAB 381-20BP. In fact CAB 381-20BP improves the alcohol resistances of all the formulations 加入CAB 381-20BP不會影響涂膜耐醇性。實際上，在所有配方中， CAB 381-20BP都可提高耐醇性 To formulate a good alcohol resistance coating, it is important to choose a low hydroxyl value and high molecular weight CAB 制定一個好的耐醇配方最重要的是選擇一個低羻基含量且高分子量的CAB * *