稀土改性脲醛树脂.doc

科毕业论文 本科毕业论文 La2O3不同加入量对脲醛树脂性能影响的研究 论文提交日期：二О一三年六月 摘 要 本论文以脲醛树脂胶粘剂的制备为基础，将不同量的氧化镧加入到脲醛树脂胶黏剂制备过程中，分析研究氧化镧改性脲醛树脂胶黏剂的各项性能指标(黏度、固化时间、固含量、游离甲醛释放量等) 的影响。实验结果显示: 不同量的氧化镧可对脲醛树脂胶黏剂的性能产生影响，本实验得出 Abstract In this thesis, the preparation of urea-formaldehyde resin adhesive, based on the different amounts of lanthanum oxide added to the urea-formaldehyde resin adhesive preparation process, analysis of lanthanum oxide modified urea formaldehyde resin adhesive performance indicators (viscosity, curing time, solid content, free formaldehyde, etc.) effects. Experimental results showed that: different amounts of lanthanum oxide urea-formaldehyde resin adhesive could affect the performance of the experiment eventually come to earth can increase viscosity, reduce the free formaldehyde content, increasing the solid content and curing time Key Words：Lanthanum oxide Urea-formaldehyde resins Modify 目 录 1 引言 1 1.1 脲醛树脂的概况 1 1.1.1 脲醛树脂的简介 1 1.1.2 脲醛树脂胶黏剂的优缺点 2 1.1.3 国内外脲醛树脂的发展现状 2 1.1.4 脲醛树脂的研究方向 3 1.2 稀土镧的简介 4 1.3 立题依据、目的、意义及研究内容 4 2 试验内容及方法 5 2.1 试验仪器和材料 5 2.2 试验配方及方案 6 2.3 改性脲醛树脂的制备方法 6 3 脲醛树脂胶的各项性能测试方法 6 3.1 粘度的测定方法 6 3.2 固含量的测定方法 7 3.3 固化时间的测定方法 7 3.4 游离甲醛含量的测定（乙酰丙酮比色法） 8 4 结果分析 9 4.1 粘度的结果分析 9 4.2 固含量的结果分析 9 4.3 固化时间的结果分析 10 4.4 游离甲醛释放量的结果分析 11 5 结论 12 致谢 13 参考文献 14 1 引言 脲醛树脂是一种尿素和甲醛缩聚而成的合成树脂，于1844年由B.Tollens首次合成，并于1929年被IG公司开发于胶接木材之后，作为胶合板与刨花板生产用胶黏剂。脲醛树脂固化后胶层无色，工艺性能好，成本低廉，并且有优良的胶接性能和较好的耐湿性，是生产人造板的主要胶种[1]。脲醛树脂应用极其广泛，既可以用于胶接木材和非木质材料，也可以用于浸渍纸张作为造板表面装饰材料，还可以用于纺织品、纸张、乐器、肥料及涂料等。可见，UF树脂胶的市场前景非常广阔。 随着人们生活水平的提高，环保意识的日益加强，因甲醛超标所带来的对身心的危害越来越受到人们的关注[2]。脲醛树脂urea-formaldehyde resins）商品名Beetle。又称尿素甲醛树脂，简称UF，平均分子量约10000。尿素与37%甲醛水溶液在酸或碱的催化下可缩聚得到线性脲粉状脲醛树脂醛低聚物，工业上以碱作催化剂，95左右反应，甲醛/尿素之摩尔比为1.5～2.0，以保证树脂能固化。反应第一步生成一和二羟甲基脲，然后羟甲基与氨基进一步缩合，得到可溶性树脂，如果用酸催化，易导致凝胶。产物需在中性条件下才能贮存。脲醛树脂主要用于制造模压塑料，制造日用生活品和电器零件，还可作板材粘合剂、纸和织物的浆料、贴面板、建筑装饰板等。[3]。液体胶能耗低，价格低，但运输费用高，销售半径小，贮存时间一般为1-2个月；粉状胶能耗高，价格高，但运输费