攀钢大方坯重轨钢用保护渣开发.doc

攀钢大方坯重轨钢用连铸保护渣开发( （1．攀枝花钢铁集团公司钢铁研究院，攀枝花 617067；2．攀枝花新钢钒股份有限公司提钒炼钢厂，四川 攀枝花 617062；3．重庆大学材料科学与工程学院，重庆 400044。） 摘 要：结合攀钢1#大方坯连铸工艺条件，进行了组份改善保护渣润滑能配模式Iron and Steel Research Institute，Panzhihua Iron and Steel Group Co.，Panzhihua 617000 ，Sichuan，China；2．Vanadium Recovery and Steelmaking Plant，Panzhihua New steel and Vanadium Co.，Ltd.，Panzhihua 617062，Sichuan，China ；3．College of Marterials Science and Engineering，Chongqing University，Chongqing 400044，China.） Abstract：In conjunction with the No.1 bloom caster process conditions in Panzhihua Iron and steel Company (PZHISC)， increas the lubricant performance and the melting homogeneous by Special contents added in mold flux were discussed as key contents，also a suitable carbon mixing was studied. Industry tests showed that the mold flux for heavy rail steels had good performance，it well meets heavy rail steels production requirements of PZHISC No.1 bloom caster. Key Words：Bloom；Heavy rail steel；Mold flux 0 引言 连铸结晶器保护渣对连铸坯质量以及连铸机产量均有重要的影响，随着人们对连铸结晶器保护渣认识的不断深入，逐渐意识到它具有不可替代的作用。从国内外方坯连铸生产实践来看，与保护渣密切相关的铸坯表面缺陷如裂纹、凹坑、结疤、夹渣等发生的频率较高，裂纹、凹坑等缺陷严重时可导致漏钢事故，影响方坯连铸产生产的顺行[1、2]。 随着攀钢提钒炼钢厂1#大方坯连铸机和2#板坯连铸机相继建成投产，实现了全连铸生产。提钒炼钢厂在引进奥钢联大方坯连铸机的同时，也进口德国斯多伯格（Stollberg）连铸保护渣，供铸机热试和考核验收期内使用。进口保护渣存在价格昂贵、供应困难等问题，由此增加生产成本，并带来管理方面的系列难题。因此，考核验收后应该有性能良好的国产连铸保护渣满足生产要求。重轨钢在攀钢1#大方坯连铸生产中占有较大比例，为此，本研究在借鉴国内外经验的基础上，结合攀钢的工艺条件，开发成功了大断面方坯重轨钢用连铸结晶器保护渣。 1 重轨钢凝固特性 攀钢提钒炼钢厂重轨钢（碳含量0.65%～0.80%）连铸钢水凝固过程具有以下特点： （1）实验表明，攀钢PD3零强度温度(ZST)较低，略超过1300℃，1300℃时试样的抗拉强度较低，为7.9Mpa，其高温塑性较差； （2）由于P、S, 拉坯过程中坯壳受到的摩擦阻力大，坯壳易与结晶器壁粘结，导致粘结漏钢； （3）坯壳与结晶器壁接触良好，传热能力强，坯壳生长较快且相对均匀，初生坯壳出现裂纹的几率较小，但坯壳之间重接能力差，在坯壳连接处容易发生拉脱甚至漏钢； （）C、P、S等偏析严重，造成铸坯内部组织成分偏析、疏松严重； （5）凝固组织基体中易出现马氏体，若冷却强度过大易出现内裂； （）Pa?s?m/min）[3]，粘度选择在0.3～0.6Pa?S，熔点控制在1080～1140℃间，以保证保护渣的消耗量。保护渣性能指标选择结果如表2所示。此外，为了在碱度较低的情况下提高保护渣熔化均匀性，除采用预熔渣型外，还利用多组分混合原理，减小分熔。因此保护渣基料的主要成分选择为CaO、MgO、SiO2、Na2O、 CaF2及特殊组分S1、S2。 表1 攀钢方坯连铸重轨钢基本工艺参数 机 型 流 数 铸机半径 /m 流间距 /m 结晶器形式 结晶器长度 /mm 多点矫直 全弧形连铸机 6 12 1.5 组合式 850 冶金长度 /m 铸坯断面 /mm×mm 设计拉速 结晶器 液位控制 结晶器 电