缓凝剂在管桩余浆制砖中的应用研究 祝健，冯蕾，朱菲菲 摘要: 本文针对管桩余浆二次利用中存在的水化时间短、利用率低等问题，通过对余浆的流动度试验，研究了两种工厂常用缓凝剂对管桩余浆应用的影响。结果表明：在温度和掺量的影响下，木镁的缓凝对余浆的缓凝效果较白糖稳定。结合企业实际情况，得出了余浆应用中缓凝剂的合理掺量，为其制砖的实际应用提供参考的依据。 Abstract: There are several problems in recycling of waste slurry of pressed concrete pipe pile, such as short hydration time and low utilization rate. In this paper, the fluidity of waste slurry in different conditions was tested and the usage of retarder was researched. The results showed that the retarding effect of magnesium lignosulfonate was more stable than that of white sugar when influenced by temperature and content. The suitable adding volume of retarder was also advised based on field production of the plant. 关键词：管桩余浆；二次利用；流动度；缓凝剂 Key words: waste slurry of pipe pile; recycling; fluidity; retarder 1引言 随着我国经济的发展，人们对建筑物的要求也越来越高，多高层到处林立，这些建筑的基础广泛采用了离心成型的预应力混凝土管桩在生产中会余浆既节约成本又减少环境污染1~4]。本文采用企业常用的白糖和木镁分别在冬季和夏季进行了不同温度下的余浆缓凝效果试验。 2试验 2.1材料 余浆：取自广天构件PHC管桩废浆；木镁及白糖：取自海曙新型建筑材料厂；混凝土砖：取自自海曙新型建筑材料厂。 2.2方法 余浆物理性能：密度采用比重瓶法测量；固含量采用烘干法；流动性：参照《GB8077-2000混凝土外加剂匀质性测试方法》。经试验同时根据工厂实际情况，规定流动度大于150mm还可以二次利用；若流动度小于150mm，则认为余浆已经失效。 余浆处理：木镁、白糖掺量按占余浆固含量的质量百分比计算。 混凝土砖强度：按JC 943-2004《混凝土多孔砖》进行试验。 3试验分析 3.1 缓凝剂不同掺量余浆缓凝效果 图1 木镁对余浆流动性的影响 图2白糖对余浆流动性的影响 图1为空白余浆和掺量分别为0.05%、0.1%和0.15%木镁的试样流动度变化。观察空白试样，经过2小时后余浆流动度下降速率明显增快，很快达到使用下限150mm；掺入0.05%木镁后，试样的拐点出现时间延缓了近120min，效果明显。当掺量达到0.10%时，余浆从取样到流动度下降为150mm的时间延长了240min。总体来看，随着时间的增长流动度变化速率加快，随着掺量的增大，流动度值变化速率变得缓慢。从试验效果来看，木镁掺量在0.05%和0.1%之间是比较适宜的。 图2为空白余浆和掺量分别为0.005%、0.010%、0. 020%、0.030%、0.040%白糖的试样流动度变化。掺入0.005%白糖的试样流动度低于空白试样的流动度，当掺量达到0.010%和0.020%时余浆前期的流动性低于空白试样，但后期的流动性比空白试样大，总体看来当掺量在0.010%时，白糖的缓凝作用明显提高，掺量达到0.020%和0.030%时，其缓凝作用反而弱于掺量为0.010%的余浆。总体上，白糖的掺量在0.010%～0.040%之间，白糖作为缓凝剂可以起到缓凝作用，但同时具有不稳定性。 3.2不同温度下缓凝剂的缓凝作用 （1）掺木镁的余浆在冬季和夏季的流动度变化分析 图3冬季木镁对余浆流动性的影响 图4夏季木镁对余浆流动性的影响 图3和图4分别为空白试样和木镁掺量为0.10%、0.15%的余浆在冬季和夏季的流动度随时间的变化。冬季木镁掺量为0.10%时，4小时之内流动度变化速率增快的拐点并没有出现，余浆还可以二次利用，在夏季大约210分钟左右出现了明显的拐点且余浆流动度下降到150mm的时间较冬季短。掺量为0.10%的试样在冬季缓凝时间达4小时，夏季缓凝时间达4.5小时，说明温度对木镁的缓凝效果的