連铸结晶器保护渣对超低碳钢增碳的影响.docVIP

连铸结晶器保护渣对超低碳钢增碳的影响 林功文　吴　杰　李正邦　　刘良田　邱同榜　陈宝云 　　摘　要　分析了连铸结晶器保护渣引起超低碳钢铸坯增碳的原因。强调指出，除了富集碳层外，含有碳的熔渣层也是引起铸坯增碳不可忽视的原因。并阐述了铸坯增碳的机理，提出了防止铸坯增碳的措施。　　关键词　超低碳钢　保护渣　富集碳层　含碳熔渣层 Effect of Flux in Continuous Casting Mold on Carbon Pick-up of Ultra-Low-Carbon Steel Lin Gongwen, Wu Jie and Li Zhengbang(Central Iron and Steel Research Institute, Beijing 100081)Liu Liangtian, Qiu Tongbang and Chen Baoyun(Wuhan Iron and Steel (Group) Corp) 　　Abstract　 The reason has been analyzed that the carbon pick-up of continuous casting slab of ultra-low-carbon steel is caused by the flux in continuous casting mold. It is