桥面水泥混凝土含水率对防水层粘结性能的影响_冯德成.docxVIP

第30卷第5期公 路 交 通科 技Vol. 30 No. 52013 年 5月Journal of Highway and Transportation Research and DevelopmentMay 2013doi:10. 3969 /j. issn. 1002 － 0268. 2013. 05. 008桥面水泥混凝土含水率对防水层粘结性能的影响冯德成，魏文鼎，詹苏涛( 哈尔滨工业大学 交通科学与工程学院，黑龙江 哈尔滨 150090)摘要: 依据表面能理论，采用柱状灯芯技术和躺滴法分别测定不同含水率时水泥混凝土与 SBS 沥青的表面能参数，并通过计算粘附功，分析了不同含水率时水泥混凝土与 SBS 沥青的粘附性。在此基础上，对水泥混凝土处于不同含水率时的层间粘结性能进行了验证。结果表明: 在含水率为 0% 时粘附功最大; 随着含水率增大，粘附功逐渐变小;随着含水率降低，防水粘结层抗剥离性能提高，当含水率降至0. 5% 后，层间粘结性能对含水率已不敏感; 随着含水率的降低，抗剪强度增大，但当含水率降至 1. 0% 后增加的幅度并不显著。关键词: 桥梁工程; 水泥混凝土含水率; 粘附功; 防水粘结层;桥面铺装中图分类号:U443. 33文献标识码: A文章编号: 1002 － 0268 ( 2013)05 － 0047 － 05Influence of Moisture Content of Cement Concrete on Performance ofWaterproof Adhesive Layer in Bridge DeckFENG De-cheng，WEI Wen-ding，ZHAN Su-tao( School of Transportation Science ＆ Engineering，Harbin Institute of Technology，Harbin Heilongjiang 150090，China)Abstract: Based on surface energy theory，the surface energy parameters of SBS asphalt and cement concrete with different moisture contents are measured by the column wicking technique and sessile drop method． Furthermore，the adhesion between cement concrete and SBS asphalt with different moisture contents is analyzed by calculating adhesion work． Then， the interlamination adhesive performance with different moisture contents is verified． The results indicate that ( 1) the adhesion work hit the maximum when moisture content is 0% ，and the adhesion work decreases gradually as moisture content increases; ( 2) as moisture content decreases，the debond resistance performance of waterproof adhesive layer improves，when the moisture content is 0. 5% ，the interlamination adhesive performance is insensitive to moisture content; ( 3) as moisture content decreases，the shear strength of waterproof adhesive layer on bridge deck also improves， but the increment is not obvious after moisture content is under 1. 0% ．Key words: bridge engineering; moisture content of cement concrete; adhesion work; waterproof adhesive layer; bridge deck沥青铺装层破坏，而且会使桥面板钢筋受到侵蚀，0引言影响桥梁结构