新型防水膜材FiberTite在金属屋面上的应用.docVIP

新型防水膜材（FiberTite）在金属屋面中的应用 尤昌懋 项 超 刘殿胜 （中国新兴建设开发总公司一公司，北京 100071） China Xinxing Construction Development General CO.，Beijing 100071，China New-style Waterproof Membrane (FiberTite) In MetalRroof Application Abstract： FiberTite waterproof membrane is one kind of new-style waterproof which has the high strength,flame retardant, durable,consecrated themselves the specific properties, such as high strength composite material that can be very good solve metal roof waterproof problems. Based on The Party School Of Central Committee Of C.P.C natatorium metal roof reconstruction project , introduces the FiberTite waterproof membrane material of material properties, construction process and quality control, etc. Key-Words：metal roof waterproof membrane material construction process detail process [摘要] FiberTite新型防水膜材具有高强、阻燃、耐久、自洁等特性的高强复合材料，膜材金属屋面防水、保温及室内网架保温、防潮、装饰。 拆除现有保温层，拆除现有金属承托铝板（更换新保温层后安装原有铝网），对现有屋架系统进行检测，根据实际情况对网架、檩条局部进行防腐处理，重新安装保温板，铺设无纺布隔离层，最后铺设外铺设FiberTite整体防水膜材。FiberTite屋面系统构造如下图所示： FiberTite屋面系统构造示意图 2、膜材的材料特性 FiberTite防水膜材料具有高强、阻燃、耐久、自洁等特性的高强复合材料，具有最高的热反射率和散热率膜材由基布和涂层二部分组成。基布主要采用高强聚脂纤维丝编织而成，平织编织方法，不同的编织方法影响着膜材料的经纬向力学性能指标，提供膜的抗拉强度和抗撕裂强度等；涂层材料主要有聚四氟乙烯和聚氯乙烯，在一定程度上提高了膜材料各项强度指标，表面硅涂层，提供膜材料的耐火、耐久及防水、自洁等性能，膜材的物理特性。代理的FiberTite-36mil型膜材，参照ASTM-美国材料与实验协会D6754-02），其主要物理性能指标见下表： 序号 物理性能 实验项目 规范最小指标 特性指标 备注 1 膜材厚度（mm） 0.79 0.91 ASTM D 751 2 纤维厚度（mm） 0.15 0.23 光学方法 3 断裂强度（N） 1175 1557 ASTM D 751 4 断裂延伸率（%） 15 18 ASTM D 751 5 抗撕裂强度（N） 335 445 ASTM D 751 6 线性空间的变化（%） 1.3 0.63 ASTM D 1204 7 纤维附着力（N/m） 225 无剥落现象 ASTM D 751 8 经56天80℃加热老化后的保留性能与原始状态的百分比 断裂强度、剥落情况 断裂伸长率、剥落情况 90% 90% 90% 90% ASTM D 3045 9 加热老化后低温弯曲 -30 -30 10 低温弯曲 -30 -30 ASTM D 2136 11 166h暴露在水中的体重变化 0.0,+6.0% 0.0,+3.7% ASTM D 471 12 出厂接缝强度（N） 1780 纤维破坏力 ASTM D 751 13 流体阻力（Mpa） 3.5 4.8 ASTM D 751 14 静态穿刺阻力 通过 通过 ASTM D 5062 15 动态穿刺阻力（J） 10 20 ASTM D 5635 16 加速风化情况 5000hr 10000hr 17 开裂 无 无 7倍放大 18 细裂纹 无 无 7倍放大 19 抗真菌，细菌持续增长情况 变色、污渍 没有生长 无 没有生长 无 20 磨损试验（圈数） 1500 1500 1K