橡胶沥青温稳定性评价标准的试验研究.docVIP

橡胶沥青高温性能评价标准的试验研究 黄卫东1，王 伟2，黄 岩3 （1.同济大学道路与交通工程教育部重点实验室, 上海； 201804. 2. 上海浦东路桥沥青材料有限公司，上海，200122；3.上海市政工程设计研究总院，上海 200092) 摘要：橡胶沥青混合料具有良好的高温稳定性，但是由于橡胶粉与基质沥青的改性机理与其他改性沥青存在较大差异，因此对于橡胶沥青高温稳定性的评价指标与标准国内尚缺乏系统的研究。通过大量的室内车辙试验，本文对胶结料的旋转粘度、软化点、针入度与橡胶沥青混合料动稳定度之间的相关性进行了试验研究。结果表明，胶结料177℃旋转粘度与软化点可作为橡胶沥青混合料高温稳定性的控制指标，但是，如果采用美国橡胶沥青的评价标准进行控制，混合料动稳定度并不能满足国内关于改性沥青的规范要求。因此，在室内试验的基础上，结合国内实际工程的经验，提出了橡胶沥青高温稳定性控制的建议标准。试验结果还显示，橡胶沥青混合料高温稳定性受到不同性质胶粉的影响很大，但是基质沥青性质差异对其的影响较其他改性沥青则相对较小。 关键词：橡胶沥青，橡胶沥青混合料，高温性能，评价指标，标准 Laboratory Study on Evaluation Criteria of AR high temperature Performance HUANG Wei-dong1, Wang Wei2, HUANG Yan3, DU Qun-le4 (1.Key Laboratory of Road and Traffic Engineering of the Ministry of Education, Tongji University, Shanghai 201804,China; 2. Shanghai Pudong Road＆bridge Asphalt-based Material Company，Shanghai 200122, China; 3. Shanghai Municipal Engineering Design Institute, Shanghai 200092,China; 4 Highway Administration Bureau of Communication Department of Hebei Province;Shijiazhuang 050051, China;) Abstract：Asphalt rubber (AR) mixtures have good high-temperature performance. The modified mechanism of AR binder is different from conventional polymer-modified asphalt (PMA). Systematic research on the evaluating index and specification for the high-temperature performance of AR is still lacked. By systematic laboratory rutting tests, the relationships between 177℃ apparent viscosity, softening point, penetration and HMA dynamic stability of AR are studied. The results indicate that the 177℃ apparent viscosity and softening point of AR binder can be used as evaluation index for the high-temperature performance. The results also indicate that the requirement for 177℃ apparent viscosity and softening point are uncritical and corresponding AR mixture rutting result may not meet the Chinese specification for PMA. So more critical requirement for 177℃ apparent viscosity and softening point are advised. The results also indicate that the high-temperature performance of the AR c