粉末冶金Fe-C-Cu-Cr-Mn组织性能研究.docxVIP

粉末冶金Fe-C-Cu-Cr-Mn组织与性能研究摘要：利用正交实验研究了铜、铬、锰含量对粉末冶金Fe-C-Cu-Cr-Mn材料烧结后组织和性能的影响。材料经冷压后于1135℃采用网带烧结炉烧结，对烧结后的材料进行了烧结密度、硬度、抗拉强度、冲击韧性测试和显微组织观察。实验结果表明：铜对硬度和抗拉强度的影响最大、铬锰次之；锰对延伸率和冲击韧性的影响最大、铜铬次之；材料烧结后的显微组织为铁素体、珠光体和孔隙。铜、铬、锰含量分别在1%-3%、0-1.2%、0.3%-1.2%变化时，Fe-0.8C-3Cu-1.2Cr-0.3Mn的综合性能最好。关键词：粉末冶金；Fe-C-Cu-Cr-Mn；组织性能The study on microstructure and properties of powder metallurgy Fe-C-Cu-Cr-MnAbstract: The copper, chromium, manganese content on the microstructure and properties of powder metallurgy Fe-C-Cu-Cr-Mn new materials was studied through orthogonal design. The materials after cold pressing was sintered by