新能源材料论文南京工业大学.doc

聚合物太阳能电池光伏材料的研究进展 班级：复材1002 学号：15 姓名：金奇杰 摘 要：聚合物太阳能电池中给体材料的能级水平、带隙、光吸收系数、溶解性、成膜性及载流子迁移率是决定器件性能的关键因素。阐述了聚合物太阳能电池中给体材料的最新研究进展，着重介绍了含有苯并双噻吩的窄带隙D－A类型的共聚物，并对一些给体材料的能级水平优化结果做了简单的总结。最后指出了未来聚合物太阳能电池给体材料今后的发展方向。 关键词：共轭聚合物；聚合物太阳能电池；窄带隙；苯并双噻吩 中图分类号：O633 文献标志码：A Recent Progress of the Photovoltaic Materials in Polymer Solar Cells Class: CM1002 SN:15 Name: Jin Qijie Abstract: The performance of devices is depend on the energy levels, bandgap, light absorption coefficient, solubility, film forming ability and carrier mobility of the donor materials in polymer solar cells. The recent progress of the in polymer solar cells is reviewed, and the containing benzo bisthien of D-A copolymers is introduced. The energy le photovoltaic materials vels optimization results of the photovoltaic materials are summarized. Furthermore, the future prospects of the photovoltaic materials in polymer solar cells are pointed out. Key words: conjugated polymer; polymer solar cells; narrow bandgap; benzo bisthien 1.引言 随着人类对能源需求的增加，能源问题成为当今社会面临的重要问题之一。由于传统化石能源的非可再生性以及人们对其利用造成大量环境污染，因此寻找一种新型的能源成为科学研究的热点。 太阳能由于污染小以及取之不尽用之不竭等优点而成为未来最有希望的清洁能源，而直接将太阳辐射能转化为电能被认为是利用太阳能的最好方式之一。目前，无机太阳能电池已占有70％左右的太阳能电池市场，但是无机太阳能电池材料的制造成本高、加工工艺复杂以及携带不方便和非柔韧性等缺点限制了其大规模应用。与无机太阳能电池相比，有机太阳能电池因具有材料来源广泛、质量轻、制备工艺简单、成本低廉及能制备大面积柔性器件等优点而成为太阳能电池新的发展方向。聚合物/富勒烯体系太阳能电池是近年来国内外研究的前沿和热点，其能量转换效率可达到8.37％[1]，但距实际应用还有一定差距，导致有机太阳能电池能量转换效率偏低的主要原因有：(1)有机材料的载流子迁移率比较低，在传输过程中电子与空穴容易发生复合；(2)材料的吸收光谱与太阳光在陆地上的波长范围不匹配，利用率偏低。传统的聚3－己基噻吩/富勒烯衍生物(P3HT/PCBM)体系存在电子能级匹配性不好(P3HT的HOMO能级太高)的问题，导致器件的开路电压较低(0.6V左右)，这限制了其能量转换效率的进一步提高，基于P3HT/PCBM体系的聚合物太阳能电池似乎也已经达到最佳的器件性能。为进一步提高能量转换效率 需要研究开发具有更好能级匹配的新材料。 受体材料基本上局限于富勒烯衍生物，而富勒烯衍生物在可见波段内对光的吸收较少。因此，为了提高聚合物太阳能电池对太阳光的吸收，作为电子给体材料应具备窄带隙、宽吸收等特点。目前，通过构筑电子给体单元与电子受体单元交替结构(D－A类型)的聚合物可以有效调节分子的能级来实现能级的调控[2]。从电子效应来看，供－吸电子单元交替相连，可以使该电子单元之间双(或叁)键的电子发生偏移，使单键具有更多的双(或叁)键特征，从而减少交替键长差，减小能隙。从分子轨道理论来解释，如图１所示，聚合物的HOMO能级与LUMO能级的位置通过给体单元和受体单元的能级位置叠加时，能提高整个分子的最高电子占据轨道(HOMO），并且降低最低电子未占据轨道 (LUMO)，从而降低聚合物的能隙，可以选择不同给受电子单体或对单体做