关于镀银层厚度.docVIP

 关于镀银层厚度，我从贾工处了解了一些信息，集合资料，现总结如下： About the thickness of the silver coating, I get some information from our expert , following is the collection of the information.  电镀性质决定镀层厚度不可能很均匀，边角处、折角处（国际上采用直径为19的球测量直径以外区域，国内用直径20的球测量直径以外区域）、深孔处等只需做到有镀层即可，不可能所有面、所有点都达到5μm以上，只能说主要面最小厚度尽量做到等于或者大于5μm，具体可参考相关电镀标准（国标或者ISO标准）。 Plating’s nature determines that the coating thickness woule not be very uniform. It is acceptable that there are coating at corners(international people measure other area with a ball of diameter 19 while domestic people measure it with a ball of diameter 20) and deep holes. Coating thichness at all faces, points will not be all thicker than 5 μ m. We can only say that we will try our best to achieve that the minimum coating thickness at major surfaces is equal to or greater than 5 μ m. And you can refer to related electroplating standard (domestic standard or ISO standard) for details. 1、镀层均匀性： thickness uniformity 所有电镀层的厚度都不会是均匀的，这是电镀的性质决定的。因为在同一个制件上，电流密度不可能做到均匀。 The coating thickness of all plating will not be uniform, this is determined by the nature of the electroplating. Because in the same product, current density might not be uniform. 不管什么电镀都是厚度不均匀,只是相差的大与小的问题,如挂镀时,每挂最上面和下面的工件肯定会比中间的厚一些,滚镀的有时一些工件滚到一些死角的地方，厚度比那些滚的流畅的工件厚度要薄一些，那单个工件来说，边角部分的厚度比中间部位的厚度要厚，这是肯定的，虽然有些厂里做了工件高区的遮挡，以免电流增大，高区烧焦，也是为了低区的厚度提升，高区厚度降低，来提升整体的厚度均匀，但是还是不可能那么均匀。这所有这些现象都是一个原因，就是电镀产品电镀时的情况就像磁铁一样有一个磁力线原理，边角或尖端的电流线是密集的，中间肯定会比边缘的少的缘故。 No matter what kind of plating it is, the thickness will not be uniform. It is just the problem whether the difference is big or small. such as the huning plating, the top and bottom of every workpiece will be thick than middle, and in rolling plating, sometimes the thickness of some blind angle is thinner than fluent rolling workpiece. It is sure that for the individual workpiece, the thickness of edge is thicker than the middle place. Although some of the factories keep the high place of workpiece be covered to avoid being burned because of t